Over the years, polyamide heat insulation strip has been widely used in glass curtain walls due to its good properties and low cost. Especially Polyamide 66 reinforced by 25% glass fiber thermal break strips, they are inserted into aluminum window, door and facade profile for thermal insulation.
The shape I thermal barrier polyamide strip can prevent the window
frame from dust and water, has a better mechanical performance, is
the first generation and easiest shape of insulating strips.
For the shape I, we can provide the following size or customize according to customers’ requirements.
Polyamide is a plastic that insulates more than 500 times better than aluminum, so thermal break profiles have a much lower Uf value – and transmit much less heat or cold. As a result, a building stays warmer in winter while keeping the heat outside more easily in summer.
Why are thermal breaks important? Thermal breaks are essential for any external modern glazing system. Thermal bridging can be responsible for up to 30% of a property's heat loss. This lowers the homes energy efficiency, leading to higher heating bills.
Item | Unit | GB/T 23615.1-2009 | BY-Technical specification |
Density | g/cm3 | 1.3±0.05 | 1.28-1.35 |
Linear expansion coefficient | K-1 | (2.3-3.5)×10-5 | (2.3-3.5)×10-5 |
Vicat softening temperature | ºC | ≥230ºC | ≥233ºC |
Melting point | ºC | ≥240 | ≥240 |
Testing for tensile cracks | - | No cracks | No cracks |
Shore hardness | - | 80±5 | 80-85 |
Impact strength(Unnotched) | KJ/m2 | ≥35 | ≥38 |
Tensile strength(longitudinal) | MPa | ≥80a | ≥82a |
Elasticity modulus | MPa | ≥4500 | ≥4550 |
Elongation at break | % | ≥2.5 | ≥2.6 |
Tensile strength(transverse) | MPa | ≥70a | ≥70a |
High temperature tensile strength(transverse) | MPa | ≥45a | ≥47a |
Low temperature tensile strength(transverse) | MPa | ≥80a | ≥81a |
Water resistance tensile strength(transverse) | MPa | ≥35a | ≥35a |
Aging resistance tensile strength(transverse) | MPa | ≥50a | ≥50a |
1. Sample water content less than 0.2% by weight.
2. Norm laboratory condition:(23±2)ºC and (50±10)% relative
humidity.
3. The specifications marked with "a" only applies to I-shape strip
otherwise, the specifications concluded between supplier and buyer
through consultation, shall be written in contract or purchase
order.
1. Expertise in the production of standard polyamide thermal break
strips.
2. Respect customers' needs, provide customized products, try best
to satisfy customers' requirements.
3. Fast service and on-time delivery
4. Strict quality control system, each production process will be
strictly supervised by us.
5.We can provide all products on the insulation strip production
line and the technical support.
Because PA66 is a hydrophilic substance, it will absorb the surrounding water. The rate and amount of water absorption depend on the ambient temperature, ambient humidity and storage period.
The relative humidity is higher in summer than in other short-term storage seasons. High moisture content (more than 2%) will affect the quality of wear-resistant strips.
When the insulation single bundle is removed from the shelf, it may be deformed. If it is not straightened in time, it will cause permanent deformation.
Therefore, it is recommended to keep it horizontal in a ventilated and dry environment, pay attention to waterproof, stay away from heat source, avoid stress and minimize bending.