Polyamide Thermal Break Strips for Hear Insulation Aluminum Profiles
The polyamide strip is a mouldable composite material. Its fibers are oriented in all three dimensions to ensure appropriate strength. As such, manufacturers can use these strips across all types of fenestration, including oversized and impact-resistant systems. Therefore, polyamide thermal barriers are the best for thermal break windows.
Over the years, polyamide heat-insulation strip has been widely used in glass curtain walls due to its good properties and low cost. Especially Polyamide 66 reinforced by 25% glass fiber thermal break strips, they are inserted into aluminum window, door and facade profile for thermal insulation.
The shape CT thermal barrier polyamide strip can prevent the window frame from dust and water. It has a better mechanical performance. It is the first generation and easiest shape of insulating strips.
For the shape CT, we can provide the following size or customize according to customers' requirements.
Currently, there are two principal types of thermal barriers: polyamide thermal barrier strip and pour & debridge (P&D).
Our company only produce polyamide thermal barrier strip.
The polyamide strip is a material of low thermal conductivity which will minimise the transfer of heat and cold through the window frame, resulting in improved energy efficiency. The polyamide strip will have a HUGE impact in reducing transfer of heat and cold over typical non-thermal profiles. These sections can be anodized or powder coated to withstand the harsh climate, including UV damage and salt corrosion.
The wider the thermal break, the greater insulation performance .
Thermally Broken windows are a major contribution to sustainable and eco-friendly homes. They help to save money, energy and support the environment.
Item | Unit | GB/T 23615.1-2009 | PW-Technical specification |
Density | g/cm3 | 1.3±0.05 | 1.28-1.35 |
Linear expansion coefficient | K-1 | (2.3-3.5)×10-5 | (2.3-3.5)×10-5 |
Vicat softening temperature | ºC | ≥230ºC | ≥233ºC |
Melting point | ºC | ≥240 | ≥240 |
Testing for tensile cracks | - | No cracks | No cracks |
Shore hardness | - | 80±5 | 80-85 |
Impact strength(Unnotched) | KJ/m2 | ≥35 | ≥38 |
Tensile strength(longitudinal) | MPa | ≥80a | ≥82a |
Elasticity modulus | MPa | ≥4500 | ≥4550 |
Elongation at break | % | ≥2.5 | ≥2.6 |
Tensile strength(transverse) | MPa | ≥70a | ≥70a |
High temperature tensile strength(transverse) | MPa | ≥45a | ≥47a |
Low temperature tensile strength(transverse) | MPa | ≥80a | ≥81a |
Water resistance tensile strength(transverse) | MPa | ≥35a | ≥35a |
Aging resistance tensile strength(transverse) | MPa | ≥50a | ≥50a |
1. Sample water content less than 0.2% by weight.
2. Norm laboratory condition:(23±2)ºC and (50±10)% relative
humidity.
3. The specifications marked with "a" only applies to I-shape strip
otherwise, the specifications concluded between supplier and buyer
through consultation, shall be written in contract or purchase
order.
Before sales
1. introduce products in detail
2. recommend suitable solutions
3. provide with reference information
During manufacturing
1. provide with layout and engineering conditions
2. inform the processing status
3. offer related documents
After Sales
1. provide installation, commissioning and training
2. offer spare parts
3. Provide with necessary technical support
Packaging details:
For all shapes, they could be packaged in linear, the length will be 6 meters, or customized.
For the Shape "I", "C" and some simple shapes, they can be packed
in rolls. 400-600 meters/roll.