Tungsten Carbide Alloy Steel Oil Drill Bit Extension Sucker Rods Cutomized Color Good Corrosion Resistance
Products Description:
Zhongshi Group provide sucker rods are designed for transmission of translational or rotational motion from ground drive to the well pump for oil extraction. The rods are round cross-section bars whose ends are provided with upset heads and thread. The rods can be rigged with various centralizers, to protect rods, couplings, and oil well tubing from wear; rods can be additionally provided with mobile scrapers for removal of paraffin deposits. "D" class sucker rods (as per API specification) display enhanced strength and anticorrosion properties, and are highly competitive in terms of quality with the products of world famous manufacturers.
Features:
1. superior-quality gree pipe and advanced heat treatment process: high strength & high toughness,especailly under low temperture
2. Smooth and long upset transition area & strong hard banding - extended product use life
3. To meet or exceed requirements of the API 5DP, API 7G, API Q1 and ISO9001
4. Equipped with advanced inspection instruments and a strictly enforced quality contrilling system, the final products are guaranteed to be superior and stable quality
5. Due to our professional technicians &product flexibility , we are capable of meeting some customer's specitic requirements
Sucker rod specification:
| Mechanical Properties Of Steel Sucker Rod | |||||||||||
| Grade | Minimum Yield Strength(0.2% Residual Deformation) | Minimum Tensile Strength | Maximum Tensile Strength | Elongation200mm% | Reduction Of Area Z% | Surface Hardness HRC | Core Hardness HB | Fatigue Life | |||
| K | 60000 | 414 | 90000 | 621 | 115000 | 793 | ≥13 | ≥50 | |||
| C | 60000 | 414 | 90000 | 621 | 115000 | 793 | ≥13 | ≥50 | |||
| D | 85000 | 586 | 115000 | 793 | 140000 | 965 | ≥13 | ≥50 | |||
| KD | 85000 | 590 | 115000 | 795 | 140000 | 965 | ≥13 | ≥50 | |||
| HL | 115000 | 795 | 140000 | 965 | 173339 | 1195 | ≥13 | ≥45 | |||
| HY | / | / | 140000 | 965 | 173339 | 1195 | / | / | ≥42 | ≥224 | |
| EHL | / | / | 188500 | 1300 | 217500 | 1500 | / | / | ≥50 | ≥320 | ≥2.5X106 |
| Note: when the yield strength cannot be measured, it should be considered to be processed into standard sample installation drawing | |||||||||||
| A: It is generally made of high quality carbon steel, which can
reach the mechanical properties of the table. B Molybdenum steel (but not limited to this type of steel) is generally used, and the mechanical properties of this table can be achieved through effective heat treatment. | |||||||||||