ASME SA335 P11 (UNS K11597) Alloy Steel Seamless Pipe For High Temperature
YUHONG GROUP deal with stainless steel seamless pipe and tube already more than 33 years, every year sell more than 80000 tons of stainless steel seamless pipe and tube. Our client already cover more than 65 countries. Our stainless steel seamless pipe and tube was width used in Mining, Energy, Petrochemical, Chemical Industry, Food plant, Paper plant, Gas and Fluid Industry etc..
Description
Alloy Steel A335 P11 Seamless Pipe Distributor, ASME SA335 Alloy Steel P11 Pipe, Stockist of UNS K11597 Alloy Steel Pipe. ASTM A335 Grade P11 is also commonly known as ASME SA335 Grade P11 Pipes, it is a seamless ferritic alloy-steel pipe that mainly has high-temperature applications. The UNS designation for this grade P11 is K11597.
The key elements of P11 pipes are carbon, manganese, phosphorous,
sulfur, silicon, chromium and molybdenum. Its key components are
chrome and moly that provide it with strength, resistance against
wear, hardenability as well as corrosion resistance properties. It
is also possible to heat treat this alloy. The chromium within the
alloy increases its resistance to oxidation allowing it to be used
in corrosive high-temperature environments. Molybdenum addition
enhances strength and wear resistance.P11 pipe material has high
toughness and high wear and tear resistance.
Chemical Composition Requirements
| ASTM A335 P11 Chemical Composition % | ||||||
| C | Mn | P | S | Si | Cr | Mo |
| 0.05-0.15 | 0.30-0.60 | ≤0.025 | ≤0.025 | 0.50-1.00 | 1.00-1.50 | 0.44-0.65 |
*C – Carbon, Mn – Manganese, P – Phosphorous, S – Sulfur, Si – Silicon, Cr-Chromium, Mo – Molybdenum.
Mechanical Properties of ASTM A335 P11
| Tensile Strength, MPa | Yield Strength, MPa | Elongation, % |
| 415 min | 205 min | 30 min |
Tensile Requirements
| Seamless | ||||||
| P-5 | P-9 | P-11 | P-22 | P-91 | P91 shall not have a hardness not exceeding 250 HB/265 HV [25HRC]. | |
| Tensile Strength, min., psi | ||||||
| ksi | 60 | 60 | 60 | 60 | 85 | |
| MPa | 415 | 415 | 415 | 415 | 585 | |
| Yield Strength, min., psi | ||||||
| ksi | 30 | 30 | 30 | 30 | 60 | |
| MPa | 205 | 205 | 205 | 205 | 415 | |
Heat Treatment, Inspection & Test
Pipes of ASTM A335 P11 may be either cold drawn or hot rolled. Each pipe shall be reheated for heat treatment – full or isothermal annealing, normalizing and tempering at a temperature no less than 1200°F(650°C).
Hydrostatic test shall be performed on each pipe length of ASTM A335 P11 along with dimensional inspection and visual examination. Longitudinal or transverse tension test, flattening test, or bend test shall be performed for each heat number of furnace. When specified by the purchaser, one of the alternative nondestructive tests can be performed: ultrasonic test, eddy current test, or flux leakage examination. Hardness test is not necessary.