SUS444 Disk Plate 8.0*1500mm Chemical Composition Sus444 Stainless
Steel Plate
SUS444 (00Cr18Mo2) is an ultra-low carbon nitrogen, 18% chromium
and 2% molybdenum, ferritic stainless steel with high corrosion
resistance. This steel is generally stabilized with niobium or
titanium, which can avoid intergranular corrosion after welding.
This steel grade is especially suitable for use in various water
treatment devices.
SUS444 steel is a high-alloy ferritic stainless steel, compared
with the commonly used steel SUS444:
1. The chromium content is about 1.0% higher, and the alloying
element molybdenum (Mo) is added, so this steel has good resistance
to pitting corrosion, crevice corrosion and stress corrosion, and
its corrosion resistance is even better than SUS304 in some fields
and SUS316.
2. Stabilizing elements such as titanium (Ti), niobium (Nb), and
zirconium (Zr) are added, so this steel has good resistance to
intergranular corrosion and high temperature oxidation.
Equivalent Material of 444 Stainless Steel plate
China | Taiwan, China | Japan | Korea | United States | ISO | European standard |
GB | ISC | CNS | JIS | KS | ASTM | UNS | | EN | No. |
| S11972 | 444 | SUS 444 | STS 444 | 444 | S44400 | X2CrMoTi18-2 | X2CrMoTi18-2 | 1.4521 |
|
specification | Thickness:0.3-6.0mm 3.0mm*100mm |
Width:500-2000mm normal size1000 1219 1220 1240 1250 1500 2000mm
Length:1000-6000mm normal size 2438 2440 3000 6000mm |
Mill | TISCO BAOSTEEL LISCO BAOXIN ZPSS JISCO |
Finish | 2b/No.1 |
Edge | Mill /raw or slit edge |
Weight | Thickness*Width*Length*7.93 per sheet |
Technique | cold rolled hot rolled |
Payment term | 30% T/T in advance,the balance before shipment |
Packing | 1.Export sea worthy package + water proof paper + wooden pallet
2.Max Loading 25mt for each 20GP container 3.Safe loading and
fixing Professional Teams |
Delivery time | Within 7-10 working days after received 30%T/T of deposit or L/C
original |
Trade terms | FOB SHANGHAI CFR&CIF your port |
Quality control | Mill Test Certificate is supplied with shipment |
444 stainless steel composition content.
Grade | C | Mn | Si | P | S | Cr | Mo | Ni | Ti |
444 Characteristic machining technology | Min. Max. | ≤0.025 | ≤1.00 | ≤1.00 | ≤0.04 | ≤0.03 | 17.5~19.5 | 1.75-2.5 | ≤0.035 | ≤0.8 |
Yield strength: ≥205 N/mm2 Tensile strength: ≥450 N/mm2 Elongation: ≥22% Hardness: HV≤200HRB≤88 |
|
444 Characteristic machining technology
1D -- The surface has discontinuous granular shape, also known as
fog surface.
Processing technology: hot rolling + annealing shot peening
pickling + cold rolling + annealing pickling.
2D - A slightly silvery white colour.
Processing technology: hot rolling + annealing shot peening
pickling + cold rolling + annealing pickling.
2B -- Silver white with better gloss and flatness than a 2D
surface.
Processing technology: hot rolling + annealing shot peening
pickling + cold rolling + annealing pickling + quenching and
tempering rolling.
Ba - Excellent surface gloss, high reflectivity, like a mirror
surface.
Processing technology: hot rolling + annealing shot peening
pickling + cold rolling + annealing pickling + surface polishing +
quenching and tempering rolling.
No.3 -- Good gloss, coarse grain surface.
Processing technology: polishing and tempering rolling for 2D or 2B
with 100~120 abrasive materials (JIS R6002).
No.4 -- Good gloss, fine lines on the surface.
Processing process: polishing and tempering rolling for 2D or 2B
with 150~180 abrasive materials (JIS R6002).
HL -- Silver grey with hair streaks.
Processing technology: 2D products or 2B products with appropriate
granularity of abrasive materials for polishing the surface is a
continuous abrasive grain.
MIRRO -- Specular.
Processing technology: 2D products or 2B products with appropriate
granularity of the grinding material grinding and polishing to the
mirror effect.
Other special surfaces: color plating, water ripple, etching,
anti-fingerprint, etc.