ASTM Standard 301 Stainless Steel Coils Sheet 3.0mm Thickness 1/2H FH

ASTM Standard 301 Stainless Steel Sheet 0.3 - 3.0mm Thickness 1/2H FH SS Sheets

Type 301 is an austenitic stainless steel alloy which offers high strength and good corrosion resistance in mildly corrosive environments at ambient temperature.

The alloy is suitable for all forms of welding and displays good ductility when cold worked. 301 stainless can also be readily formed and drawn. Type 301L is the low carbon version of Type 301 and is suitable for applications which require good ductility. High strength combined with excellent corrosion resistance makes 301 stainless ideal for a wide range of applications in sectors such as aerospace, rail and automotive.

Type 301 Stainless Steel, often referred to as UNS S30100, is a popular austenitic chromium-nickel stainless steel that is known for its corrosion resistance. Similar to Type 304, Type 301 has lower levels of chromium and nickel which increases its cold work-hardening range.

Type 301 is readily formed and drawn and is has good weldability. It is utilized for a wide variety of applications and industries including:

• Aircraft parts
• Truck and trailer bodies
• Kitchen utensils and table wear
• Architectural (trim, drainage products, storm door frames)
• Automotive (trim, wheel, covers)
• Conveyor Belts
• Home and industrial appliances
• Mass transit systems

Type 301 Stainless Steel has a minimum tensile strength of 185,000 PSI and 140,000 PSI yield strength. All the Type 301 stainless steel we supply meets or exceeds the industry’s toughest standards.

PROPERTIES: ANNEALED CONDITION

Ultimate Tensile Strength: 75 KSI min (930 MPA min) Yield Strength: (0.2% offset): 30 KSI min (205 MPA min) Elongation: 40% Min Hardness: B92 or Equiv. Max

PROPERTIES: TEMPERED

1/16 Hard Ultimate Tensile Strength: 90 KSI min (629 MPA min) Yield Strength: (0.2% Offset) 45 KSI min (310 MPA min) Elongation: 40% Min 1/8 Hard Ultimate Tensile Strength: 100 KSI min (690 MPA) Yield Strength: (0.2% Offset) 55 KSI min/380 MPA min Elongation: 40% Min1/4 Hard Ultimate Tensile Strength: 125 KSI min (860 MPA) Yield Strength: (0.2% Offset) 75 KSI min/930 MPA min Elongation: 25% Min

1/2 Hard Ultimate Tensile Strength: 150 KSI min (1035 MPA min) Yield Strength: (0.2% Offset) 110 KSI min (760 MPA min) Elongation: 15%<.015" 18%>.015" 3/4 Hard Ultimate Tensile Strength: 175 KSI min (1205 MPA min) Yield Strength: (0.2% Offset) 135 KSI MIN/930 MPA MIN Elongation: 10%< .015" 12%> .015" Full Hard Ultimate Tensile Strength: 185 KSI min (1275 MPA min) Yield Strength: (0.2% Offset) 140 KSI min (965 MPA min) Elongation: 8% < .015" 9% > .015" Extra Full Hard Ultimate Tensile Strength: 270 KSI min< .014" (1860 MPA min) 250 KSI min .015" to 017" (1720 MPA min) 225 KSI min .0171" to .019" (1552 MPA min) 205 KSI min .0191 to .021 (1435 MPA min) 185 KSI min >.0211 (1275 MPA min) Spring Tempered Ultimate Tensile Strength: 185 KSI min (1275 MPA min) Yield Strength: (0.2% Offset) 140 KSI min (965 MPA min) Elongation: 8% < .015" 9% > .045"