1.6511 Alloy Steel Pipe Tube SMLS Pipe ASTM DIN Standard SCH160S Heavy Wall Pipe
Product Name | Carbon Steel Pipe; Carbon Steel Tube | |||
A36; A106B; A113; A131; A283;A284; A306; A335; A573; SS400; SAE1006; SAE1008; SAE1010; 1020; 1015; 4001; 4130; 4140; 4340 Q195; Q215; Q235B; Q255; Q275; Q345B; Q420; Q460; Q550; Q690; S275JR; S355JR; S40C; S45C; S50; S55C; 65Mn; T8; T10; T8A; T10A; T12A 10#; 20#; 35#;45#; etc. | ||||
square: 10*10-1000*1000mm rectangular: 10*15 - 800*1100mm Round:10.3mm-609mm | ||||
Thickness | 0.25-100mm or customization | |||
Length | 1-12m or customization | |||
Protection | Plastic caps | |||
Pipe Ends | plain, beveled, threaded, socket with holes, with PVC clap/
coupling/ clamp or as customers' requirement | |||
Lead Time | 7-15 days | |||
Technique | Hot Rolled/Cold Rolled/Cold Drawn | |||
Quality Certificate | ISO 9001 | |||
liquid delivery (pump well, gas, water) construction pipe structural pipe(greenhouse structure, fence post) boiler pipe(Resistance to high pressure)Oil casing (Drilling for oil) Precision tube(Machine parts) | ||||
1.6511|36CrNiMo4 alloy Steel is a high quality Quenched and Tempered Alloy Structural steel, It belong to the high quality medium carbon, Oil Quenched & Tempered Hardenss is 28-34 HRc. 1.6511|36CrNiMo4 Annealing delivery hardenss less than 250HB.
Din W-Nr 1.6511|36CrNiMo4 Alloy structural steel properties is very simliar with GB 40CrNiMo steel, JIS SNCM439 and ASTM 4340 Alloy structural steel. At most work environment, 1.6511|36CrNiMo4 is equivalent with 40CrNiMo steel, 4340 steel, SNCM439 steel.
Related Specifications ASTM A29/A29M DIN EN 10083/3 JIS G4053 GB GB/T 3077
Form of Supply
Din W-Nr 1.6511|36CrNiMo4 Alloy structural steel, we can supply the 4340 round bar, steel flat bar, plate, hexagonal steel bar and steel square block. Din W-Nr 1.6511|36CrNiMo4 steel Round bar can be sawn to your required lengths as one offs or multiple cut pieces. Din W-Nr 1.6511|36CrNiMo4 Rectangular pieces can be sawn from flat bar or plate to your specific sizes. Ground tool steel bar can be supplied, providing a quality precision finished bar to tight tolerances.
Chemical composition
| C(％) | 0.38～0.43 | Si(％) | 0.15～0.35 | Mn(％) | 0.60～0.80 | P(％) | ≤0.035 |
| S(％) | ≤0.040 | Cr(％) | 0.70～0.90 | Mo(％) | 0.20～0.30 | Ni(%) | 1.65～2.00 |
Heat treatment Related
Slowly heated to 650-700 ℃ and allow enough times, let the steel to be thoroughly heated, Then cool slowly in the furnace. The 1.6511| 36CrNiMo4 steel will get MAX 250 HB (Brinell hardness).
Heated slowly to 850-880°C,Keep about 2 hours.Then cool in air.
Heated slowly to 820-860°C, Then after adequate soaking at this temperature quench in oil.
Heated to 540-680°C, Keep at the temperature for 2 hours per 25mm of section, then allow to cool in air.
Mechanical Properties in Hardening and Tempering Condition
| Diameter (mm) | 0.2 % proof stress (N/mm2) | Tensile strength (N/mm2) | Elongation (%) | Reduction of area (%) | Notch impact energy (J) |
| <16 | 900 | 1100-1300 | 10 | 45 | 40 |
| 17-40 | 800 | 1000-1200 | 11 | 50 | 45 |
| 41-100 | 700 | 900-1100 | 12 | 55 | 50 |
| 101-160 | 600 | 800-950 | 13 | 60 | 50 |
| 161-250 | 550 | 750-900 | 14 | 60 | 50 |
Applications
For permanently stressed components with large cross sections for automotive and mechanical engineering. For economic performance under severe dynamic stress, parts must be designed for optimum strength or toughness. Din W-Nr 1.6511|36CrNiMo4 steel is a quenched and tempered (Q+T) alloy structural steel, is used for engineering structural, Used as require good toughness, high strength, as well as the important conditioning of large size, heavy machinery such as high load of axial, turbine shaft, larger than 250 mm in diameter of helicopter rotor shaft, turbojet engine turbine shaft, blade, high load of transmission parts, fasteners of the crankshaft. Gear, etc.; 1.6511 also be used for operating temperature over 400 ℃ of rotor shaft and blade, etc.; And after nitriding processing can also be used to make special performance requirements of the important parts, after low temperature tempering or can be used for ultra-high strength steel after isothermal quenching
Regular size and Tolerance
| 1) Hot Rolled round bar | |||
| Diameter (mm) | Diameter Tolerance (mm) | Diameter (mm) | Diameter Tolerance (mm) |
| ≤12.70 | -0.13 ～0.30 | >50.80～63.5 | -0.25～0.76 |
| 12.7～25.40 | -0.13～0.41 | >63.50～76.20 | -0.25～1.02 |
| >25.4～38.10 | -0.15～0.51 | >76.20～101.60 | -0.30～+1.27 |
| >38.1～50.80 | -0.20～0.64 | >101.60～203.20 | -0.38～3.81 |
| 2) Hot Rolled steel plate | |||
| Thickness (mm) | Thickness Tolerance (mm) | Thickness (mm) | Thickness Tolerance (mm) |
| ≤25.4 | -0.41～0.79 | >127～152 | -1.60～2.39 |
| >25.4～76 | -0.79～1.19 | >178～254 | -1.98～3.18 |
| >76～127 | -1.19～1.60 | >254～305 | -2.39～3.96 |