ASTM A789 Duplex S32520 Stainless Steel Seamless Pipe for Heat Exchanger and Petroleum Industry
Products Name | UNS S32520 Stainless Steel Pipe |
Pipe Type | Seamless Pipe . Welded Pipe |
Surface | Pickling , polishing |
Out Diameter | 6 - 508mm |
Wall Thickness | 1.0 - 50.0mm |
Length | 6m or cutting any length as request |
Standard | ASTM / GB / EN / DIN / JIS / BS / BIS |
Mainly Grade | 304 304L 304H 309S 310S 316L 316Ti 317L 321 347 2205 2507 904L 254SMO 800/800H Alloy20 ,Hastelloy Alloy, Monel Alloy,Inconel Alloy |
Service | Cutting, Polishing, Hairline Finishing |
MOQ | 200 Kgs |
Packing | standard packing for export |
Application | Industrial , food , medical, househould |
ASME SA 789 UNS 32520 Duplex Steel Pipe for Heat Exchanger and petroleum industry
Duplex stainless steel has a signatory dual microstructure phase, which gives them heightened advantages in comparison to conventional steel. And since the ductility factor of these alloys is high, achieving an ASTM A789 UNS 32520 Duplex Stainless Steel Pipe Brighting Annealing is relatively simple. As bright annealed bars, not only do they have a smooth surface but, they can be constructed by the manufacturers, despite tight tolerances. Buyers have the option of purchasing either seamless or welded duplex steel pipes. Though with regards to its appearance, both welded and an ASME SA 789 UNS 32520 Seamless Pipe may be similar, yet dissimilar. While the shape and size of the pipe may be similar, the manner of manufacturing the UNS S32550 grade F61 Welded Pipe involves a weld seam. Though it is possible to redact the appearance of a weld seam by a significant degree, in a high pressured environment, the performance of a welded pipe is almost 20% lower than that of a seamless one. Yet, the cost-efficiency of a welded type is much higher than the former. When one speaks of the properties of duplex stainless steel alloys - their corrosion resistance is a feature that suits corrosive applications. Not to forget their performance in stress-related corrosive environments, where conventional alloys are susceptible to cracking. Cracked pipes are highly undesired in applications, where the media transported is flammable or toxic. Toxic media is highly corrosive. Either gaseous or liquid, the media flowing through pipes causes some form of friction. As the durability, corrosion resistance, and longevity of Alloy F255 UNS 32520 Pipe is much higher many buyers prefer using them. The specifications as - ASTM A790 and ASTM A789, are used in the construction of UNS S32520 EN 1.4507 Duplex Pipe. Both specifications take into consideration seamless as well as welded constructed pipes. In addition to the chemistry requirements, both specifications - ASTM A789 and ASTM A790 UNS S32520 Pipe require conformance to tests about their mechanical properties.
ASTM A789 UNS 32520 Seamless Pipe
ASTM A789 UNS 32520 Welded Pipe
UNS DESIGNATION | AMERICAN (USA) SPECIFICATION |
---|---|
UNS S31803 | ASTM A789/ SA789 |
UNS S32205 | ASTM A789/ SA789 |
UNS S31500 | ASTM A789/ SA789 |
UNS S32550 | ASTM A789/ SA789 |
UNS S32750 | ASTM A789/ SA789 |
UNS S32950 | ASTM A789/ SA789 |
UNS S32520 | ASTM A789/ SA789 |
UNS DESIGNATION | COMPOSITION, % | ||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|
C MAX | MN MAX | P MAX | S MAX | SI MAX | NI | CR | MO | N | CU | OTHERS | |
S31803 | 0.03 | 2 | 0.03 | 0.02 | 1 | 4.5-6.5 | 21.0-23.0 | 2.5-3.5 | 0.08-0.20 | . . . | . . . |
S32205 | 0.03 | 2 | 0.03 | 0.02 | 1 | 4.5-6.5 | 22-23 | 3.0-3.5 | 0.14-0.20 | . . . | . . . |
S31500 | 0.03 | 1.20-2.00 | 0.03 | 0.03 | 1.40-2.0 | 4.3-5.2 | 18-19 | 2.5-3.0 | 0.05-0.10 | . . . | . . . |
S32550 | 0.04 | 1.5 | 0.04 | 0.03 | 1 | 4.5-6.5 | 24-27 | 2.9-3.9 | 0.10-0.25 | 1.50-2.50 | . . . |
S31200 | 0.03 | 2 | 0.045 | 0.03 | 1 | 5.5-6.5 | 24-26 | 1.-2.0 | 0.14-0.20 | . . . | . . . |
S31260 | 0.03 | 1 | 0.03 | 0.03 | 0.75 | 5.5-7.5 | 24-26 | 2.5-3.5 | 0.10-0.30 | 0.20-0.80 | W 0.10-0.50 |
S32001 | 0.03 | 4.0-6.0 | 0.04 | 0.03 | 1 | 1.0-3.0 | 19.5-21.5 | 0.6 | 0.05-0.17 | 1.00 max | . . . |
S32304 | 0.03 | 2.5 | 0.04 | 0.04 | 1 | 3.0-5.5 | 21.5-24.5 | 0.05-0.60 | 0.05-0.20 | 0.05-0.60 | . . . |
S32750 | 0.03 | 1.2 | 0.035 | 0.02 | 0.8 | 6.0-8.0 | 24-26 | 3.0-5.0 | 0.24-0.32 | 0.50max | . . . |
S32760 | 0.05 | 1 | 0.03 | 0.01 | 1 | 6.0-8.0 | 24-26 | 3.0-4.0 | 0.20-0.30 | 0.50-1.00 | W 0.50-1.00 |
S32950 | 0.03 | 2 | 0.035 | 0.01 | 0.6 | 3.5-5.2 | 26-29 | 1.0-2.5 | 0.15-0.35 | . . . | . . . |
S32520 | 0.03 | 1.5 | 0.035 | 0.02 | 0.8 | 5.5-8.0 | 23-25 | 3.0-5.0 | 0.20-0.35 | 0.8 | . . . |
DUPLEX GRADE | TENSILE STRENGTH, MIN., KSI [MPA] | YIELD STRENGTH, MIN., KSI [MPA] | ELONGATION IN 2 IN., OR 50MM, MIN, % | HARDNESS, MAX BRINELL |
---|---|---|---|---|
S31803 | 90 [620] | 65 [450] | 25 | 290 |
S32205 | 95 [655] | 70 [485] | 25 | 290 |
S31500 | 92 [630] | 64 [440] | 30 | 290 |
S32550 | 110 [760] | 80 [550] | 15 | 297 |
S31200 | 100 [690] | 65 [450] | 25 | 280 |
S31260 | 100 [690] | 65 [450] | 25 | 290 |
S32001 | 90 [620] | 65 [450] | 25 | 290 |
S32304 | 100 [690] | 65 [450] | 25 | 290 |
S32750 | 116 [800] | 80 [550] | 15 | 310 |
S32760 | 109 [750] | 80 [550] | 25 | 300 |
S32950 | 100 [690] | 70 [480] | 20 | 290 |
S32520 | 112 [770] | 80 [550] | 25 |