301 Stainless Steel Strip 1/2H Tensile Strength>1035Mpa Thickness 0.15 - 3.0mm
| Product Name | Stainless Steel Strips |
| Length | As required |
| Width | 3mm-1219mm or as required |
| Thickness | 0.15 - 3.0mm or as required |
| Standard | AISI,ASTM,DIN,JIS,GB,JIS,SUS,EN,etc. |
| Technique | Hot rolled / cold rolled |
| Surface Treatment | 2B or according to customer requirement |
| Thickness tolerance | ±0.01mm |
| Material | 201, 202, 301, 302, 303, 304, 304L, 304H, 310S, 316, 316L, 317L, 321,310S 309S, 410, 410S,420, 430, 431, 440A,904L |
| Application | It is widely used in high temperature applications, medical devices, building materials, chemistry, food industry, agriculture, ship components.It also applies to food, beverage packaging, kitchen supplies, trains, aircraft, conveyor belts, vehicles, bolts, nuts, springs, and screen. |
| MOQ | 1tons.We also can accept sample order. |
| Shipment time | Within 15-20 workdays after receiving deposit or L/C |
| Export packing | Waterproof paper, and steel strip packed.Standard Export Seaworthy Package.Suit for all kinds of transport,or as required |
| Capacity | 250,000 tons/year |
AISI 301 stainless steel (UNS S30100) is the most susceptible to cold deformation strengthening among conventional austenitic stainless steels. Its work hardening rate is extremely high, with each increase in the amount of cold work, the tensile strength and yield strength will increase significantly. The response to work hardening is particularly important for structural parts, including angle steel and channel sections, which are expected to have additional strength and stiffness after manufacture. On the other hand, for deep drawing applications, lower work hardening rates are generally preferred and can be obtained in austenitic alloys with higher nickel content (especially types 304, 304L, and 305).
| ASTM | AISI (UNS) | C, ≤ | Si, ≤ | Mn, ≤ | P, ≤ | S, ≤ | Cr | Ni | Mo, ≤ | Cu, ≤ | N, ≤ |
| ASTM A240/A240M; | 301 (UNS S30100) | 0.15 | 1.00 | 2.00 | 0.045 | 0.03 | 16.0-18.0 | 6.0-8.0 | – | – | 0.1 |
Standard of our 301 stainless steel strips
AISI 301 stainless steel mechanical properties are given in the datasheet below including tensile strength, yield strength, elongation, reduction in area, Brinell and Rockwell hardness, etc.
| Type 301 Mechanical Properties | |||||||
| ASTM | AISI Type (UNS) | Conditions | Tensile Strength, MPa (ksi), ≥ | 0.2% Yield Strength, MPa (ksi), ≥ | Elongation in 50 mm (2 in.), %, ≥ | Brinell Hardness (HB), ≤ | Rockwell Hardness (HRB), ≤ |
| ASTM A666 | 301 (UNS S30100) | Annealed | 517 (75) | 205 (30) | 40 | 217 | 95 |
| Full Hard | 1275 (185) | 965 (140) | 8 (<0.015 in.); 9 (≥ 0.015 in) | ||||
| Super Full Hard | 1860 (270) | 1790 (260) | – | ||||
| Half Hard | 1035 (150) | 760 (110) | 15 (<0.015 in); 18 (≥ 0.015 in) | ||||
| 3/4 Hard | 1205 (175) | 930 (135) | 10 (<0.015 in); 12 (≥ 0.015 in) | ||||
| 1/4 (quarter-hard) Hard | 862 (125) | 517 (75) | 25 | ||||
| 1/8 Hard | 690 (100) | 380 (55) | 40 | ||||
| 1/16 Hard | 620 (90) | 310 (45) | 40 | ||||
| SAE AMS 5517 | 18Cr-8Ni (SAE 30301 ) | – | 862 (125) | 517 (75) | 25 | 252, ≥ | 25 HRC, ≥ |
Grade 301 stainless steel equivalent to Chinese GB, ISO, Japanese JIS, and European EN standard (Germany DIN EN, British BSI…).
| ASTM | European | China | Japan | ISO | ||
| 301 (UNS S30100) | 1.4310 | 1Cr17Ni7; 12Cr17Ni7 | SUS301 | ISO 15510 | X5CrNi17-7 (4319-301-00-I) | |
Type 301 have been extensively used in coining of spoons and forks, other applications include springs, fasteners, clamps, automotive wheel covers, aircraft structural parts, etc.