Cold Rolled 2B 2D BA Surface Stainless Steel Strips 0.1 - 2.0mm Thickness SS Strip
Product Name | Stainless Steel Strips |
Length | As required |
Width | 3mm-1219mm or as required |
Thickness | 0.1 - 3.0mm or as required |
Standard | AISI,ASTM,DIN,JIS,GB,JIS,SUS,EN,etc. |
Technique | Hot rolled / cold rolled |
Surface Treatment | 2B or according to customer requirement |
Thickness tolerance | ±0.01mm |
Material | 201, 202, 301, 302, 303, 304, 304L, 304H, 310S, 316, 316L, 317L, 321,310S 309S, 410, 410S,420, 430, 431, 440A,904L |
MOQ | 1tons.We also can accept sample order. |
Shipment time | Within 15-20 workdays after receiving deposit or L/C |
Export packing | Waterproof paper, and steel strip packed.Standard Export Seaworthy Package.Suit for all kinds of transport,or as required |
Capacity | 2500 tons/year |
Product Name | 316/316L Stainless Steel Strip |
Equivalent Grade | 316: AISI 316, UNS S31600, SAE 316, DIN 1.4401, SUS 316, X5CrNiMo17-12-2 |
316L: AISI 316L, UNS S31603, SAE 316L, DIN 1.4404, SUS 316L, X2CrNiMo17-12-2 | |
Standard | GB, AISI, ASTM, DIN, EN, JIS |
Process | Hot Rolled, Cold Rolled |
Sizes | Thickness: 0.1-3.0mm, Width: 10-600mm |
Surface Treatment | NO.1, 2B, NO.4, BA, HL, Mirror |
Packing | Wooden Pallet |
Certificate | EN 10204-3.1 |
Chemical Composition of 316L Stainless Steel Strips
C | Mn | P | S | Si | Cr | Ni | Mo | N | Cu | |
316 | 0.08 | 2.00 | 0.045 | 0.03 | 0.75 | 16.00-18.00 | 10.00-14.00 | 2.00-3.00 | 0.10 | / |
316L | 0.03 | 2.00 | 0.045 | 0.03 | 0.75 | 16.00-18.00 | 10.00-14.00 | 2.00-3.00 | 0.10 | / |
Tensile Strength (min) | Yield Strength (min) | Elongation | Hardness, max | ||||
ksi | Mpa | ksi | Mpa | / | Brinell.HBW | Rockwell | |
316 | 75 | 515 | 30 | 205 | 40 | 217 | 95HRBW |
316L | 70 | 485 | 25 | 170 | 40 | 217 | 95HRBW |
Cold Rolled & Hot Rolled Stainless Steel Strips
Cold rolling refers to a rolling process that uses the pressure of rolls to squeeze steel to change the shape of the steel at room temperature. The advantafe of cold rolling is fast forming speed, high output, the coating is not damaged, and it can be made into a variety of cross-sectional forms to meet the needs of the use conditions. In addition, cold rolling can cause large plastic deformation of the steel, thereby increasing the yield point of the steel. Which is Widely used in home appliances and other industries.
Hot rolling is a metalworking process. Such as steel ingots or billets are difficult to deform and process at room temperature, they are generally heated to 1100 to 1250° for rolling, this rolling process is called hot rolling. Most steel materials are rolled by hot rolling, the steel delivered in the hot-rolled state has a certain degree of corrosion resistance due to the high temperature, so it can bestored in the open air. In addition, hot rolling is that it can destroy the casting structure of the ingot, refine the grain of the steel, eliminate structural defects, make the steel structure dense, and improve the hardness of the hot rolled steel.
Surface Detail of our stainless steel strip