AISI 1065 Carbon Steel (UNS G10650) Spring Steel Strip Width 10 - 1250mm
Specification of our products
Product Name | Cold rolled steel strip |
Thickness | 0.12-4mm |
Coil Weight | 3-8 ton, or as your requirement |
width | 6-700mm, or as your requirement |
Tolerance | Thickness: +/-0.02mm, Width:+/-2mm |
Material grade | 65MN S50C, C50, CK50, CK50E, SAE 1050 S75C, C75, CK75, CK75E, SAE1075 S60C, C60, CK60, CK60E, SAE1060 S45C, C45, CK45, CK45E, SAE1045 S55C, C55, CK55, CK55E, SAE1055 SK4, SK5, SK85,51CrV4, 75Cr1 60Si2Mn, 55Si2Mn, 62Si2Mn, SUP 6,etc |
surface | iron gray (low carbon plate), brown (special alloy plate, the high
carbon plate), partial ochre (weather resistance), with temperature
oxidation pattern, than manufacture rough surface |
Standard | ASTM,DIN,JIS,BS,GB/T |
Payment terms | 30% T/T deposit in advance, 70% T/T balance within 5 days after B/L
copy, 100% Irrevocable L/C at sight, 100% Irrevocable L/C after receive B/L 30-120 days, etc |
Delivery times | Delivered within 7 days after the receipt of deposit |
Package | tied up with steel strips and wrapped with water proof paper |
Application Range | Widely used in ship, automobile, Bridges, buildings, machinery,
pressure vessels and other manufacturing industries |
Advantages | 1. Reasonable price with excellent quality 2. Abundant stock and prompt delivery 3. Rich supply and export experience, sincere service |
Certificates | CE, ISO9001-2008,ETC. |
Steels containing carbon as the major alloying element are called carbon steels. They may also contain up to 1.2% manganese and 0.4% silicon. Residual elements such as copper, molybdenum, aluminium, chromium and nickel are also present in these steels.
AISI 1065 carbon steel is a high-carbon steel, which has high tensile strength and heat treatable.
The following sections will give an overview of AISI 1065 carbon steel in detail.
The chemical composition of AISI 1065 carbon steel is outlined in the following table.
| Element | Content (%) |
|---|---|
| Iron, Fe | 98.31 - 98.8 |
| Manganese, Mn | 0.60 - 0.90 |
| Carbon, C | 0.60 - 0.70 |
| Sulfur, S | 0.05 |
| Phosphorous, P | 0.04 |
The physical properties of AISI 1065 carbon steel are tabulated below.
| Properties | Metric | Imperial |
|---|---|---|
| Density | 7.85 g/cm3 | 0.284 lb/in³ |
The following table shows mechanical properties of cold drawn AISI 1065 carbon steel.
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength, ultimate | 635 MPa | 92100 psi |
| Tensile strength, yield | 490 MPa | 71100 psi |
| Modulus of elasticity | 200 GPa | 29007 ksi |
| Bulk modulus (typical for steel) | 140 GPa | 20300 ksi |
| Shear modulus (typical for steel) | 80 GPa | 11600 ksi |
| Poissons ratio (typical for steel) | 0.27-0.30 | 0.27-0.30 |
| Elongation at break (in 50 mm) | 10% | 10% |
| Reduction of area | 45% | 45% |
| Hardness, Brinell | 187 | 187 |
| Hardness, Knoop (converted from Brinell hardness) | 209 | 209 |
| Hardness, Rockwell B (converted from Brinell hardness) | 90 | 90 |
| Hardness, Rockwell C (converted from Brinell hardness. Value below normal HRC range, for comparison purposes only) | 10 | 10 |
| Hardness, Vickers (converted from Brinell hardness) | 196 | 196 |
| Machinability (based on AISI 1212 steel. as 100 machinability) | 60 | 60 |
The thermal properties of AISI 1065 carbon steel are given in the following table.
| Properties | Metric | Imperial |
|---|---|---|
| Thermal conductivity | 49.8 W/mK | 346 BTU in/hr.ft².°F |
Other designations that are equivalent to AISI 1065 carbon steel include the following: