EN 1.4529 / UNS N08926 Nickel Alloy Seamless Pipe Tube Custom Cutting Any Length

EN 1.4529 / UNS N08926 Nickel Alloy Seamless Pipe Tube Custom Cutting Any Length

What is Incoloy 926?

The Cr content in nickel-based alloy incoloy 926 is usually 14.0 – 18.0 %, the nickel content is 24.0 – 26.0%. Incoloy 926 (UNS N08926) is a nickel-based alloy containing titanium and aluminum. It contains enough chromium to form and maintain a sufficient scale of chromium oxide to protect it under high temperature conditions. It is more resistant to high temperature than traditional chromium-nickel stainless steel such as 304; The higher nickel content makes it have better oxidation resistance than the standard 18-8 stainless steel, and its oxidation resistance is not inferior to the higher grades whose service temperature is as high as 1900 °F (1038 °C) alloy.

Chemical composition (%) of nickel-based alloy incoloy 926 (UNS N08926)

Mechanical Properties of nickel-based alloy incoloy 926 (UNS N08926/W.Nr.1.4529)

Characteristic of nickel-based alloy incoloy 926 (UNS N08926/W.Nr.1.4529)

• 1. It has high resistance to pitting and crevice corrosion when in Halide and H2S contained acid media.
• 2. In practice, effective in resistance of chloride stress corrosion cracking.
• 3. A variety of corrosion have good corrosion resistance capability in the normal oxidation and restore environment.
• 4.Upgrade mechanical properties than Cronifer 1925 LC – Alloy 904 L.
• 5. Alloys has Improved the stability of metallurgical compared to a range of 18% of the nickel content alloys.
• 6. With a certification of applied in manufacturing-related pressure vessel (VdTUV -196 – 400 ℃ and ASME )

Processing and heat treatment of incoloy 926 (UNS N08926/W.Nr.1.4529)

Incoloy 926 nickel-based alloy is suitable for cold and hot processing and machining, but due to its high strength, cold and hot processing requires high-power processing equipment.

Heating of Incoloy 926 (UNS N08926/W.Nr.1.4529)

• (1) Keep the workpiece clean before and during heat treatment.
• (2) Do not touch sulfur, phosphorus, lead and other low melting point metals during the heat treatment process, otherwise it will damage the performance of the material. Care should be taken to remove dirt such as marking paint, temperature indicating paint, colored crayons, lubricating oil, fuel, etc.
• (3) The lower the sulfur content in the fuel, the better. The sulfur content in natural gas should be less than 0.1 %, and the sulfur content in heavy oil should be less than 0.5%.
• (4) Considering the need for temperature control and keeping clean, it is best to conduct heat treatment in a vacuum furnace or a gas shielded furnace.
• (5) It can also be heated in a box furnace or a gas furnace, but the furnace gas must be clean and neutral to slightly oxidizing. The furnace gas should be avoided from fluctuating between oxidizing and reducing properties. The heating flame cannot be directly heated. Burn to the workpiece.

Application areas of nickel-based alloy incoloy 926 (UNS N08926/W.Nr.1.4529)

Incoloy 926 (N08926) alloy is a multi-purpose material, which can be used in many industrial fields:

• Fire system, water purification system, marine engineering and hydraulic piping perfusion system.
• The pipeline, joint, air systems in the acidic gas production.
• Evaporator, the heat exchanger, filter, mixer, etc. in the phosphate production.
• Power plants condensation and pipe system in the use of sewage water to cool water.
• The use of acidic organic catalyst chlorinated derivatives production.
• The production of cellulose pulp,Polished bar in the orrosive oil wells.
• Hose system in the oceanngineering,Flue gas desulphurization system components.
• Sulfuric acid condensation and separation system,Crystalline salt concentration and the evaporator.
• Transport of corrosive chemicals containers,Reverse osmosis desalination plan.
• Heat exchange tubes
• Pipe fittings
• Flanges
• Valves