JIANGSU MITTEL STEEL INDUSTRIAL LIMITED |
Verified Suppliers
|
|
Products | Stainless Steel Plate |
Thickness | 0.6 - 60.0mm |
Width | 1000mm 1219mm 1500mm 1800mm 2000mm or other width as request |
Length | 2000mm 2438mm 3000mm 6000mm or other length as request |
Grade | 201 202 301 304 304L 304H 309S 310S 316L 316Ti 317L 321 347 409L 410 420 430 431 436L 439 441 443 444 2205 2507 904L 600 625 800 825 718 253MA 254SMO.etc |
Service | Laser Cutting, Surface processing, bending |
Brand | TISCO BAOSTEEL POSCO LISCO JISCO |
Standard | ASTM JIS GB DIN EN BS |
Certificate | ISO MTC C/O F/E |
Packing | Wooden pallets and waterproof paper |
Deliver time | 5 - 15 days |
Loading port | Shanghai Port |
Our 304 Stainless Steel Sheet & Plate in Stock
304 Stainless Steel Plate & Sheet in Stock | |||
0.3*1219*2438 | 3.0*1500*6000mm | 30*1500*6000mm | 0.3*1000*2000mm |
0.4*1219*2438 | 4.0*1500*6000mm | 35*1500*6000mm | 0.4*1000*2000mm |
0.5*1219*2438 | 5.0*1500*6000mm | 40*1500*6000mm | 0.5*1000*2000mm |
0.6*1219*2438 | 6.0*1500*6000mm | 45*1500*6000mm | 0.6*1000*2000mm |
0.8*1219*2438 | 8.0*1500*6000mm | 50*1500*6000mm | 0.8*1000*2000mm |
1.0*1219*2438 | 10.0*1500*6000mm | 55*1500*6000mm | 1.0*1000*2000mm |
1.2*1219*2438 | 12.0*1500*6000mm | 60*1500*6000mm | 1.2*1000*2000mm |
1.5*1219*2438 | 14.0*1500*6000mm | 65*1500*6000mm | 1.5*1000*2000mm |
2.0*1219*2438 | 16.0*1500*6000mm | 70*1500*6000mm | 2.0*1000*2000mm |
2.5*1219*2438 | 20.0*1500*6000mm | 75*1500*6000mm | 2.5*1000*2000mm |
3.0*1219*2438 | 25.0*1500*6000mm | 80*1500*6000mm | 3.0*1000*2000mm |
304 Stainless Steel Plate with 1800mm 2000mm Width
3.0*1800*6000mm | 5.0*2000*6000mm |
4.0*1800*6000mm | 6.0*2000*6000mm |
5.0*1800*6000mm | 8.0*2000*6000mm |
6.0*1800*6000mm | 10.0*2000*6000mm |
8.0*1800*6000mm | 12.0*2000*6000mm |
10.0*1800*6000mm | 14.0*2000*6000mm |
3.0*2000*6000mm | 16.0*2000*6000mm |
4.0*2000*6000mm | 20-60*2000*6000mm |
AISI 304 (1.4301) is a widely-used austenitic chromium-nickel stainless steel. It has excellent drawing properties and very good formability, while it is also highly corrosion-resistant. Typical uses of 304 stainless steel include sinks, kitchen equipment such as pans, tubing and much more.
Type 304 is sometimes also referred to as 18/8, a moniker that comes from its typical composition of 18% chromium and 8% nickel. Other elements in the alloy include nickel, manganese, silicon, nitrogen, carbon, phosphorus, and sulphur.
AISI 304 typically contains 17.5-19.5% chromium, 8-10.5% nickel, 2% manganese, 1% silicon, 0.11% nitrogen, 0.07% carbon, 0.05% phosphorus, and 0.03% sulphur.
Table 1. Chemical composition of AISI 304 stainless steel
Element | Weight |
Iron | 66.74 - 71.24% (Balance) |
Chromium | 17.5 - 19.5% |
Nickel | 8 - 10.5% |
Manganese | 2% |
Silicon | 1% |
Nitrogen | 0.11% |
Carbon | 0.07% |
Phosphorus | 0.05% |
Sulphur | 0.03% |
The table below shows some of the most common material properties of AISI 304.
304 (Typical values at 20°C) | 304 Annealed (Typical values at 20°C) | |
Density | 8 g/cm³ | |
Elastic modulus | 193 GPa | 200 GPa |
Hardness, Brinell | 215 HB | |
Tensile strength | 500-700 MPa | 590 MPa |
Yield strength | 190 MPa | 240 MPa |
Elongation | 40% | |
Coefficient of thermal expansion | 1.72E-5 1/K | |
Thermal conductivity | 16.2 W/(m·K) | |
Melting point | 1450°C | |
Specific heat capacity | 500 J/(kg·K) | |
Electrical resistivity | 0.73 x 106 Ω·m |