Hot Rolled 316L Stainless STeel Plate 0.5 - 60.0mm SS Plate 1.4404
/ AISI316L Stainless
Product name | 316L Stainless steel plate |
Standard | GB,JIS,DIN,AISI,ASTM,AISI,ASME |
Thickness | 1.5mm-50mm |
Width | 1000,1219,1250,1500mm, or as your requirements |
Length | 2000,2438,2500,3000,6000mm, or as your requirements |
MOQ | 1MT |
Surface | No.1, 2B, BA, 8K Mirror, Hairline,satin,
Embossed,brush,No.4,HL,matt,pvc film,laser film. |
Packing | standard export packing (inside:water proof paper,outside:steel
covered with strips and pallets) |
Cargo ready date | within 25-35 days after confirming orders |
Delivery Time | About 5-7 days after receive the deposit. |
ASTM A240 316/316l Stainless Steel Plate
In ASTM A240, type 316 and 316L is a chromium nickel austenitic
steel, Element molybdenum addition can enhances corrosion
resistance of stainless steel, which is the main factor that
316/316l is more corrosion resistant than 304/304l. When 316L steel
of low carbon content is only a little higher than 316 steel on
strength level. So sometimes grade 316l is almost the same as 316
grade. Another difference, 316l can be used for weld treatment as
it contains lower carbon.
316/316L steel has outstanding corrosion resistant properties,
whether it is atmospheric or oxidizing environment, even for marine
atmosphere, it shows excellent corrosion resistance in welded
state. Normally 316/316l steel shows no magnetic in annealed
condition, cold drawn or cold rolling process may make it with
little magnetic, and it can be fixed with further processing.
Applications of ASTM A240 316/316L
316/316L plate is used to manufacture products for applications
that are exposed to salt water, acids such as sulfuric acid and
chloride, petrochemicals and chemicals and high-heat such as
engines and motors.Products include tanks, supports and frames,
enclosures and housings, engine, motor and machinery components and
parts.
Chemical Composition of 316/316L Steel Plate
Chemical Composition of 316/316L steel |
---|
Element | 316 | 316L |
---|
Carbon | 0.08 | 0.030 max |
Chromium | 16.0-18.0 | 16.0-18.0 |
Nickel | 10.0-14.0 | 10.0-14.0 |
Molybdenum | 2.00-3.00 | 2.00-3.00 |
Manganese | 2.00 | 2.00 |
Silicon | 0.75 | 0.75 |
Nitrogen | 0.10 | 0.10 |
Phosphorus | 0.045 | 0.045 |
Sulfur | 0.030 | 0.030 |
Mechanical Properties of 316/316L Steel Plate
Mechanical Property of 316/316l | 316 | 316L |
---|
Yield Strength, min. (ksi) | 30 | 25 |
Tensile Strength, min. (ksi) | 75 | 70 |
Elongation, min. (%) | 40 | 40 |
Hardness, max. (Rb) | 95 | 95 |
Stainless Steel Standards of 316/316L steel
Steel Standards of 316/316L |
---|
316 | 316L |
---|
ASTM A240 | ASTM A240 |
ASTM A666 | ASTM A666 |
ASME SA240 | ASME SA240 |
AMS 5524 | AMS 5507 |