Welded sanitary stainless tubing Mirror Finish For Food / Dairy Industry
ASTM A270 sanitary (hygienic) stainless steel tubing is the standard specification for the welded seamless, and heavily cold worked welded austenitic and ferritic stainless steel sanitary tubing. It includes the stainless steel tube types in seamless and welded ERW, EFW. ASTM A270 sanitary tubing intended applied in the diary and food industry, bio processing equipment, and having special surface finish.
ASTM A270 sanitary stainless pipe usually refers to the small pipe
diameters, normally from 1/2” to 2 1/2”, thickness from 0.049 in
(1.24mm) to 0.15 in (3.81mm).
The maximum outer diameter of ASTM A270 tubing is 12 inches (304.8
mm).
ASTM A270 tubing using inch-pound as the standard unit of measure.
Wall thickness tolerance shall not vary more than 12.5%.
Manufacturing to: ASTM A269, DIN 17458/EN10216-5 TC1 (D4/T3) NACE MR.01.75/77, Cert. To EN 10204 3.1
Test: 100% Eddy Test & Hydrostatic Test
Delivery Condition: Annealed & Pickled, Annealed & Pickled + Polished, Bright
Annealed
Outside Diameter: 6mm-101.6mm, Wall Thickness: 1mm-8mm
Material Grade: TP304/304L/304H, 316/316L, 321/321H, 317/317L, 347/347H, 309S, 310S, 2205, 2507, 904L (1.4301, 1.4306, 1.4948, 1.4401, 1.4404, 1.4571, 1.4541, 1.4833, 1.4878, 1.4550, 1.4462, 1.4438, 1.4845)
Every Tubes is inspected for all around quality & meticulous inspection insures that every tube to be best quality & total compliance with its respective standards.
Advantage:
• Advanced production and inspection equipment
• Top quality control system and service system
• Professional & Sincerity
• Competitive Price
• Good Reputation
• Timely Delivery
| SIZE | OD MM | THK MM |
| 1" | 25.0 | 1.20 |
| 1 1/4" | 32.0 | 1.20 |
| 1 1/2" | 38.0 | 1.20 |
| 2" | 51.0 | 1.20 |
| 2 1/2" | 63.5 | 1.60 |
| 3" | 76.1 | 1.60 |
| 4" | 101.6 | 2.00 |
Chemical Element Analysis
| Type | Chemical Composition(%) | |||||||||
| ASTM | C | Cr | Ni | Mn | P | S | Mo | Si | Cu | N |
| TP304 | ≤0.08 | 18.0-20.0 | 8.0-11.0 | ≤2.00 | ≤0.045 | ≤0.030 | - - - | ≤1.00 | - - - | - - - |
| TP304L | ≤0.035 | 18.0-20.0 | 8.0-13.0 | ≤2.00 | ≤0.045 | ≤0.030 | - - - | ≤1.00 | - - - | - - - |
| TP304H | 0.04-0.10 | 18.0-20.0 | 8.0-11.0 | ≤2.00 | ≤0.045 | ≤0.030 | - - - | ≤1.00 | - - - | - - - |
| TP310S | ≤0.08 | 24.0-26.0 | 19.0-22.0 | ≤2.00 | ≤0.045 | ≤0.030 | ≤0.75 | ≤1.00 | - - - | - - - |
| TP316 | ≤0.08 | 16.0-18.0 | 11.0-14.0 | ≤2.00 | ≤0.045 | ≤0.030 | 2.00-3.00 | ≤1.00 | - - - | - - - |
| TP316L | ≤0.035 | 16.0-18.0 | 10.0-14.0 | ≤2.00 | ≤0.045 | ≤0.030 | 2.00-3.00 | ≤1.00 | - - - | - - - |
| TP316N | ≤0.08 | 16.0-18.0 | 11.0-14.0 | ≤2.00 | ≤0.045 | ≤0.030 | 2.00-3.00 | ≤1.00 | - - - | 0.10-0.16 |
| TP317L | ≤0.035 | 18.0-20.0 | 11.0-15.0 | ≤2.00 | ≤0.045 | ≤0.030 | 3.0-4.0 | ≤1.00 | - - - | - - - |
| TP321 | ≤0.08 | 17.0-19.0 | 9.0-12.0 | ≤2.00 | ≤0.045 | ≤0.030 | - - - | ≤1.00 | - - - | ≤0.10 |
| TP321H | 0.04-0.10 | 17.0-19.0 | 9.0-12.0 | ≤2.00 | ≤0.045 | ≤0.030 | - - - | ≤1.00 | - - - | - - - |
| TP347 | ≤0.08 | 17.0-19.0 | 9.0-13.0 | ≤2.00 | ≤0.045 | ≤0.030 | - - - | ≤1.00 | - - - | - - - |