Welding duplex stainless steel grade 2205 Tubing 5/8 Inch x1.2mmx20ft OD 8mm-1000mm
Specifications:
UNS S31803
ASME SA-182 (F51), SA-240, SA-798, SA-790, SA-815
ASTM A182 (F51),A240, A276, A479, A789, A790, A815, A928, A988
SAE J405
UNS S32205
ASME SA-182 (F60), SA-240, SA-798, SA-790, SA-815
ASTM A182 (F60), A240, A276, A479, A480, A798, A790, A815, A928,
A988
SAE J405
Specifications of Duplex Stainless Steel Welded Tube
1. Standard: ASTM ASME
2. Grade: 630 / 631 / 2205 / 2507 / 17-4PH
ASTM A789, ASTM A790, ASTM A450, ASTM A530,
GB/T 14976, GB/T 14975, GB/T 13296, etc
3. OD: 8mm-1000mm
4. Wall thickness: 0.3mm-30mm
5. Length: max.18000mm or as demand
6. Surface finish: Polishing (180#,220#,240#,320#400#,600#), Hairline, acid pickled, etc.
2205 is a duplex (austenitic-ferritic) stainless steel containing
about 40 - 50% ferrite in the annealed condition. 2205 has been a
practical solution to chloride stress corrosion cracking problems
experienced with 304/304L or 316/316L stainless. The high chromium,
molybdenum and nitrogen contents provide corrosion resistance
superior to 316/316L and 317L stainless in most environments. 2205
is not suggested for operating temperatures above 600°F.
The design strength of 2205 is significantly higher than 316/316L,
often permitting lighter wall construction. 2205 has good notch
impact toughness down to temperatures below - 40°F. 2205 is welded
with E2209 or ER2209 fillers.
Features
| Specifications (ASTM/ASME) Duplex Stainless Steel Pipe | ||||
| Alloy | UNS Designation | Material Specification | Tubing Specification | Pipe Specification |
| 2205 | S31803/S32205 | A 240/SA-240 | A 270 | A 790/SA-790 |
| A 789/SA-789 | A928/SA928 | |||
Chemical Compositions:
| Chemical Composition (%) Duplex Stainless Steel Pipe | ||
| Alloy | 2205 | 2205 |
| UNS Designation | S31803 | S32205 |
| Carbon (C) max. | 0.030 | 0.030 |
| Manganese (Mn) max. | 2.00 | 2.00 |
| Phosphorus (P) max. | 0.030 | 0.030 |
| Sulfur (S) max. | 0.020 | 0.020 |
| Silicon (Si) max. | 1.00 | 1.00 |
| Chromium (Cr) | 21.0 - 23.0 | 22.0 - 23.0 |
| Nickel (Ni) | 4.5 - 6.5 | 4.5 - 6.5 |
| Molybdenum (Mo) | 2.5 - 3.5 | 3.0 - 3.5 |
| Nitrogen (N) | 0.08 - 0.20 | 0.14 - 0.20 |
| Iron (Fe) | Balance | Balance |
ASTM A789 UNS S31803 Tube Specification:
| Chemical Element | % Present |
|---|---|
| Carbon (C) | 0.0 – 0.03 |
| Chromium (Cr) | 21.00 – 23.00 |
| Manganese (Mn) | 2.00 max |
| Silicon (Si) | 1.00 max |
| Phosphorous (P) | 0.0 – 0.03 |
| Sulphur (S) | 0.0 – 0.02 |
| Nickel (Ni) | 4.50 – 6.50 |
| Nitrogen (N) | 0.08 – 0.20 |
| Molybdenum (Mo) | 2.50 – 3.50 |
| Iron (Fe) | Balance |
| Physical Property | Value |
|---|---|
| Density | 7.805 g/cm³ |
| Thermal Expansion | 13.7 x10^-6 /K |
| Modulus of Elasticity | 200 GPa |
| Thermal Conductivity | 19.0 W/m.K |
| Electrical Resistivity | 0.085 x10^-6 Ω .m |
| Mechanical Property | Value |
|---|---|
| Proof Stress | 450 Min MPa |
| Tensile Strength | 620 Min MPa |
| Elongation A50 mm | 25 Min % |
| Hardness Brinell | 290 Max HB |