SA268 TP405 S40500 Stainless Steel Tube Ferritic Stainless Steel Tubing
TP405
Product Description: TP405 Stainless Steel Seamless tubes and pipes
1) Commodity name: TP405 Stainless Steel Seamless Tubes and Pipes
2) Process method: Cold rolled/ cold drawn
3) Surface finish: Annealed/ pickled
4) Material: TP405
5) Standards: ASTM, GB, DIN, JIS, GOST
6) Size:
A) O. D.: Φ 6 to Φ 273mm
B)W. T: 0.5-25mm
7) Length: Max. 16 meters (specific or random)
8) Delivery conditions: Annealed, pickled
Spezilla's seamless bright annealed stainless steel tubes are
produced acc. to the following process and inspection to assure our
quality:
1. Chemical Composition Analysis Test With 100% PMI.
2. Solution Annealing / Bright Annealed.
3. 100% Hydrostatic Test and 100% Eddy Current Test
4. Mechanical Tests includes Tension Test, Flattening Test, Flaring
Test, Hardness Test.
5. Impact Test subject to Standard request.
6. Grain Size Test and Intergranular Corrosion Test.
7. Visual Test and Endoscope Test for Surface Quality Test
| Item Code: | TP405 |
| Tube OD.: | 1/4'' - 2'' |
| Wall: | 0.028'' - 0.120'' |
| Length: | 20FT |
| Material: | 405 |
| Standard: | ASTM A268 ASME SA268 |
| Finish: | Annealed & Pickled. |
| Type: | Seamless Cold Drawn |
| Certification: | ISO9001:2015 |
| Mill Test Certificate: | EN10204 3.1 |
| Packing: | Sleeved, Wooden Boxed |
Applications
405 is the perfect grade stainless steel to be used in
automotive applications where visual appeal is not a top priority.
For this reason and for its durability to gas corrosion,
405 is most commonly used in truck exhaust systems,
agricultural equipment, and heat and gas turbine exhaust silencers.
Typical Manufacturing Specifications:
ASTM A268
ASME SA268
Features
Although susceptible to rust formation, making this grade of
stainless steel somewhat undesirable for decorative purposes, 409
is extremely resistant to various forms of gas corrosion.
Magnetic Properties: 409 flat rolled stainless steel is magnetic
and cannot be hardened by heat treatment. It can, however, be
somewhat hardened by cold-working. Type 405 has great
ductility and is suitable for use in deep draw applications.
It is also easily formable.
Chemical Composition
The chemical composition of grade 405 stainless steel is outlined
in the following table.
| Element | Content (%) |
|---|---|
| Iron, Fe | 85 |
| Chromium, Cr | 13 |
| Manganese, Mn | 1.0 |
| Silicon, Si | 1.0 |
| Aluminum, Al | 0.2 |
| Carbon, C | 0.080 |
| Phosphorous, P | 0.040 |
| Sulfur, S | 0.030 |
Physical Properties The following table shows the physical
properties of grade 405 stainless steel.
| Properties | Metric | Imperial |
|---|---|---|
| Density | 7.80 g/cm 3 | 0.282 lb/in³ |
Mechanical Properties The mechanical properties of grade 405
annealed stainless steel are displayed in the following table.
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength | 448 MPa | 65000 psi |
| Yield strength (@strain 0.200 %/) | 276 MPa | 40000 psi |
| Elastic modulus | 200 GPa | 29007 ksi |
| Poisson's ratio | 0.27-0.30 | 0.27-0.30 |
| Elongation at break (in 50 mm) | 25.00% | 25.00% |
| Izod Impact (@20°C/68°F) | 41.0 J | 30.2 ft-lb |
| Hardness, Brinell (converted from Rockwell B hardness) | 131 | 131 |
| Hardness, Knoop (converted from Rockwell B hardness) | 146 | 146 |
| Hardness, Rockwell B | 75 | 75 |
| Hardness, Vickers (converted from Rockwell B hardness) | 140 | 140 |
| Grade: | TP405 | TP410 | TP249 | TP430 | TP443 | TP446-1 | TP446-2 | … | TP409 |
| UNS | S40500 | S41000 | S42900 | S43000 | S44300 | S44600 | S44600 | S40800 | S40900 |
| C, max | 0.08 | 0.15 | 0.12 | 0.12 | 0.20 | 0.20 | 0.12 | 0.08 | 0.08 |
| Mn,max | 1.00 | 1.00 | 1.00 | 1.00 | 1.00 | 1.50 | 1.50 | 1.00 | 1.00 |
| P, max | 0.04 | 0.04 | 0.04 | 0.04 | 0.04 | 0.04 | 0.04 | 0.045 | 0.045 |
| S, max | 0.03 | 0.03 | 0.03 | 0.03 | 0.03 | 0.03 | 0.03 | 0.045 | 0.045 |
| Si, max | 1.00 | 1.00 | 1.00 | 1.00 | 1.00 | 1.00 | 1.00 | 1.00 | 1.00 |
| Ni | 0.50max | … | … | … | 0.75max | 0.75max | 0.50max | 0.80max | 0.50max |
| Cr | 11.5-14.5 | 11.5-13.5 | 14.0-16.0 | 16.0-18.0 | 18.0-23.0 | 23.0-27.0 | 23.0-27.0 | 11.5-13.0 | 10.5-11.7 |
| Mo | … | … | … | … | … | … | … | … | … |
| Al | 0.10-0.30 | … | … | … | … | … | … | … | … |
| Cu | … | … | … | … | 0.90-1.25 | … | … | … | … |
| N | … | … | … | … | … | 0.25 | 0.25 | 12xCmin | 6xCmin |
| Ti | … | … | … | … | … | … | … | 1.10max | 0.75max |