ISO9001 Galvanized Steel Square Tubing s235jr welded 2 inch q195
Hot-dip galvanized pipe is to make the molten metal react with the iron matrix to produce an alloy layer,so that the matrix and the coating are combined.Hot-dip galvanizing is to pickle the steel pipe first.In order to remove the iron oxide on the surface of the steel pipe, after pickling,it is cleaned in the tank of ammonium chloride or zinc chloride aqueous solution or mixed aqueous solutionof ammonium chloride and zinc chloride, and then sent to the in the hot dip bath. |
Product Name | Galvanized Steel Pipe/Tube |
Thickness | 0.1mm-300mm or as required |
Standard | AISI,ASTM,DIN,JIS,GB,JIS,SUS,EN,etc. |
Technique | Cold rolled |
Surface Treatment | Clean, blasting and painting according to customer requirement |
Thickness tolerance | ±0.15mm |
Material | Q345,Q345A,Q345B,Q345C,Q345D,Q345E,Q235B HC340LA,HC380LA,HC420LA B340LA,B410LA 15CRMO,12Cr1MoV,20CR,40CR,65MN A709GR50 |
Coatings | Top Coats :5 micron primer + 20 micron colour Back Coat: 5 micron
primer - 7 micron primer |
MOQ | 1tons.We also can accept sample order. |
Shipment time | Within 15-20 workdays after receiving deposit or L/C |
Export packing | Waterproof paper, and steel strip packed. Standard Export Seaworthy Package.Suit for all kinds of transport,or as required |
Chemical Composition
| Specification | Grade | Chemical Composition(wt%) | ||||||
| C | Mn | Ni | Cr | Mo | Ti | |||
| ASTMJIS | 316L/022Cr17Ni12Mo2 | ≤0.03 | ≤2.0 | 10.0-14.0 | 16.0-18.0 | 2.0-3.0 | - | |
| JIS | SUS316L | ≤0.03 | ≤2.0 | 12.0-15.0 | 16.0-18.0 | 2.0-3.0 | - | |
| ASTMJIS | 316Ti/SUS 316Ti | ≤0.08 | ≤2.0 | 10.0-14.0 | 16.0-18.0 | 2.0-3.0 | 5*(C+N)-0.7 | |
Properties
| Spec | Grade | Mechanical Property | Physical Property | ||||
Y.S (N/MM2) | T.S (N/MM2) | EL (%) | HRB | Specific Heat (J/g℃) | Modulus of Elasticity (KN/mm2) | ||
| ASTM/GB | 316L/022Cr17Ni12Mo2 | ≥170 | ≥485 | ≥40 | ≤95 | 0.5 | 193 |
| JIS | SUS316L | ≥175 | ≥480 | ≥40 | ≤90 | 193 | |
| ASTM | 316Ti | ≥205 | ≥515 | ≥40 | ≤95 | 0.5 | 200 |
Applications:316L: Widely used in corrosion-susceptible environment and some mechanical components those are difficult to make heat treatment after forming in more corrosive environment.316Ti: Mainly used for industrial components. |