High Temperature 310S Metal Stainless Steel Sheet With NO 1 Surface

High Temperature 310S Stainless Steel Sheet with NO.1 Surface
 
Product Description

• Item: High Temperature 310S Stainless Steel Sheet with NO.1 Surface
• Standard: ASTM A240,ASTM A480,ASTM A167,ASTM A176
• Material: 201,202,301,304,304L,304N,XM21,304LN,305,309S,310S,316,316Ti,316L,316N,316LN,317,317L,321,347,329,405,409,430,434,444,403,410,420,440A,etc.
• Specifications:
• Thickness: 0.01-200mm
• Width: 1m,1.22m,1.5m and 1.8m.
• Length: 2m,2.44m,5.8m,6m.
• Surface: No.1, 2B, BA, NO.4, 8K mirror, checkered, embossed, hair line, sand blast, Brush, etching, etc.

What is 310S stainless steel?

310S stainless steel is austenitic chromium-nickel stainless steel, which has good oxidation resistance, corrosion resistance, and high temperature resistance. Because of the higher percentage of chromium and nickel, it has much better creep strength and can continue to work at high temperatures. Has good high temperature resistance. Due to the high content of nickel (Ni) and chromium (Cr), it has good oxidation resistance, corrosion resistance, acid and alkali resistance, and high temperature resistance. High temperature resistant steel pipes are specially used for the manufacture of electric furnace tubes and other occasions. After the content, due to its solid solution strengthening effect to improve the strength, the chemical composition of austenitic stainless steel is based on the addition of molybdenum, tungsten, niobium and titanium based on chromium and nickel. Therefore, it has high strength and creep strength at high temperature. Melting point is 1470 ° C, 800 ° C begins to soften, and allowable stress continues to decrease.

310S Chemical Composition

310S Mechanical Properties

Surface

 
1D—The surface has discontinuous particles, which is also called matte. Processing technology: hot rolling + annealing shot peening pickling + cold rolling + annealing pickling.
2D—Slightly shiny silver-white. Processing technology: hot rolling + annealing shot peening pickling + cold rolling + annealing pickling.
2B—Silver white and better gloss and flatness than 2D surface. Processing technology: hot rolling + annealing shot peening pickling + cold rolling + annealing pickling + quenching and tempering rolling.
BA—The surface gloss is excellent and has a high reflectivity, just like the mirror surface. Processing technology: hot rolling + annealing shot peening pickling + cold rolling + annealing pickling + surface polishing + quenched and tempered rolling.
No.3—has better gloss and rough surface. Processing technology: Polishing and tempering rolling of 2D products or 2B with 100 ~ 120 abrasive materials.
No.4—has better gloss and fine lines on the surface. Processing technology: Polishing and tempering rolling of 2D products or 2B with 150 ~ 180 abrasive materials.
HL—Silver gray with hair streaks. Processing technology: Polish the 2D product or 2B product with a suitable size of abrasive material to make the surface appear continuous grain.
MIRROR—is in a mirror state. Processing technology: 2D or 2B products are ground and polished to a mirror effect with a suitable abrasive material.
 
 

Grade Table for stainless steel  