Silicone rubber MCSIL-2088 is a two-component material, consisting of Part A base silicone and Part B MCSIL-C520, cures at room temperature by a condensation reaction.

Features of Artificial Stone Mould Making Silicone Rubber Stone And Tile Concrete Molds

lGood flow ability and long working time

lMedium hardness

lHigh tear and tensile strength

lEasy de-mould from complex replica parts

lAcid and alkali-resistance

lLow linear shrinkage

TDS of Artificial Stone Mould Making Silicone Rubber Stone And Tile Concrete Molds

How to make the silicone mold?

• The surface of the original should be clean and free of loose material. If your products with thin flower patterns, and especially with porous substrates, pls use a suitable mold release agent such as soap water, detergent, Vaseline or petroleum jelly.
• Mixing

Please weight 100 Part A base and 2 parts of B the Curing Agent in a clean container. Thoroughly stir Part A base silicone before use, as filler separation may occur upon prolonged storage. Mixing Part A and Part B evenly until the CA30 completely dispersed in the base. Hand or mechanical mixing can be used, but do not for an extended period of time or allow the temperature to exceed 35C (95F). Mix suitably small quantities to ensure thorough mixing of base and curing agent.

It is strongly recommended that entrapped air be removed in a vacuum chamber, allowing the mix to completely expand and then collapse. After a further 1-2 minutes under vacuum, the mix should be inspected and can be used if free of air bubbles. A volume increase of 3-5 times will occur on vacuum de-airing the mixture. So a suitably large container should be chosen.

Pouring the mixture and curing

Pour the mixed Part A base silicone and part B the curing agent as soon as possible onto the original, avoiding air entrapment. The catalyzed material will cure to a flexible rubber within 6 hours (or faster by different mixing ratio or room temperature), we advice you de-mold after 24 hours, it is will improve the replicate times of silicone mold.

Storge of Artificial Stone Mould Making Silicone Rubber Stone And Tile Concrete Molds

When the silicone rubber is stored at or below 30 centi degree in the original unopened containers, RTV2 Silicone Base and CA30 Curing agent have a usable life of 10 months from the date of production. After 10 months stockpiles use the Stir to mix the Part A silicone for some minutes, then the silicone can be use again, no influence for other performance.