MINGCHENG GROUP LIMITED |
Verified Suppliers
|
|
Description
Clear silicone rubber addition cure shore 40 Silicone Rubber for
molding will reproduce the finest detail and is suitable for a
variety of industrial and art related applications including
prototypes, furniture, sculpture and architectural elements. RTV2
Silicone can also be used to cast a variety of materials including
wax, gypsum, low melt alloys/metals and urethane, epoxy or
polyester resins.
Typical properties of Addition Cure 40 Shore A Transparent Liquid Silicone Rubber:
Item No. | MCPLA-H40 |
Color | Transparent |
Mixing ratio | 10:1 |
Mixed viscosity | 50000±300cps |
Pot life | 60 mins |
Curing time | 24 Hours |
Hardness | 40Shore A |
Tear Strength | 16 N/mm |
Tensile Strength | 3.8 Mpa |
Elongation at break | 350% |
Shrinkage | 0.10% |
All the datasheet just for reference, we can produce silicone as
per your request.
Important
The platinum catalyst is contained in component B.
Caution
Only components A and B that have the same lot number may be
processed together!
To ensure both optimum flow and homogeneity of the material, the
components must be stirred thoroughly before they are removed or
processed in their containers, in order to uniformly disperse any
fillers that might have settled during storage.
Packaging of Addition Cure 40 Shore A Transparent Liquid Silicone Rubber:
Part A base silicone: 20kg/drum, or 200kg/drum
Storage of Addition Cure 40 Shore A Transparent Liquid Silicone Rubber:
When the silicone rubber is stored at or below 30 centi degree in the original unopened containers, Silicone Base and Curing agent have a usable life of 10 months from the date of production. After 10 months stockpiles use the Stir to mix the Part A silicone for some minutes, then the silicone can be use again, no influence for other performance.
We are manufacturer, and specialized in manufacturing different hardness, different viscosity silicone rubber series, we are competitive in price with good quality.
Any question, welcome to contact us for further discussion.