Characteristics of cold rolled stainless steel
1. Cold-rolled stainless steel plate is stainless steel plate produced by cold-rolled process.The thickness is generally 1.5-4.0mm.
2. Cold-rolled plate: high strength, high hardness, high surface finish, generally as a sheet, can be used as a bronzing plate.
3.Cold-rolled stainless steel plates can not only form a special
texture pattern on the surface.Also can improve the strength
and flatness of stainless steel plate.
| Product Name | Stainless Steel Coil |
| Material | 200,300,400 |
| Thickness | 0.12MM-18MM |
| Width | 1219-3000MM |
| Length | 1250-11800MM |
| Fabrication service | Slit cut, average into smaller coil and so on |
| Inspection | Fully accept all the third party to test before shipment. |
| Standard | JIS, AiSi, ASTM, GB, DIN, EN |
| Packing | Standard Export Seaworthy Package.Suit for all kinds of transport,or as required. |
| Payment Term | TT / LC |
Stainless Steel Surface Treatments
1D—The surface has discontinuous particles, which is also called
matte. Processing technology: hot rolling + annealing shot peening
pickling + cold rolling + annealing pickling.
2D—Slightly shiny silver-white. Processing technology: hot rolling
+ annealing shot peening pickling + cold rolling + annealing
pickling.
2B—Silver white and better gloss and flatness than 2D surface.
Processing technology: hot rolling + annealing shot peening
pickling + cold rolling + annealing pickling + quenching and
tempering rolling.
BA—The surface gloss is excellent and has a high reflectivity, just
like the mirror surface. Processing technology: hot rolling +
annealing shot peening pickling + cold rolling + annealing pickling
+ surface polishing + quenched and tempered rolling.
No.3—has better gloss and rough surface. Processing technology:
Polishing and tempering rolling of 2D products or 2B with 100 ~ 120
abrasive materials.
No.4—has better gloss and fine lines on the surface. Processing
technology: Polishing and tempering rolling of 2D products or 2B
with 150 ~ 180 abrasive materials.
HL—Silver gray with hair streaks. Processing technology: Polish the
2D product or 2B product with a suitable size of abrasive material
to make the surface appear continuous grain.
MIRROR Machining —is in a mirror state. Processing technology: 2D
or 2B products are ground and polished to a mirror effect with a
suitable abrasive material.
| Surface Finish | Definition | Application |
| 2B | Those finished, after cold rolling, by heat treatment, pickling or other equivalent treatment and lastly by cold rolling to given appropriate luster. | Medical equipment, Food industry, Construction material, Kitchen utensils. |
| BA | Those processed with bright heat treatment after cold rolling. | Kitchen utensils, Electric equipment, Building construction. |
| NO.3 | Those finished by polishing with No.100 to No.120 abrasives specified in JIS R6001. | Kitchen utensils, Building construction. |
| NO.4 | Those finished by polishing with No.150 to No.180 abrasives specified in JIS R6001. | Kitchen utensils, Building construction, Medical equipment. |
| HL | Those finished polishing so as to give continuous polishing streaks by using abrasive of suitable grain size. | Building construction |
| NO.1 | The surface finished by heat treatment and pickling or processes corresponding there to after hot rolling. | Chemical tank, pipe. |
Corresponding photo of stainless steel surface treatment
Stainless Steel Composition Contents Proportion Table
| 200 series | |||||||||||||
| Grade | chemical composition (%) | mechanic performances | |||||||||||
| C | Si | Mn | P | S | Ni | Cr | N | Cu | Y.S(N/mm2) | T.S(N/mm2) | Elog(%) | HRB | |
| 201(1%nickel) | ≤0.15 | ≤1.00 | 8∽11 | ≤0.060 | ≤0.030 | 0.9∽1.5 | 15∽17 | ≤0.25 | 1.5∽2 | ≥310 | ≥655 | ≥35 | ≤105 |
| 202(4%nickel) | ≤0.15 | ≤1.00 | 6∽9 | ≤0.060 | ≤0.030 | 3.5∽5 | 15∽17 | ≤0.25 | 1.5∽2 | ≥260 | ≥620 | ≥40 | ≤100 |
| The specification of type 201&202 in conformity with Mill Standard | |||||||||||||
| 300 series | |||||||||||||
| Grade | chemical composition (%) | mechanic performances | |||||||||||
| C | Si | Mn | P | S | Ni | Cr | Mo | Y.S(N/mm2) | T.S(N/mm2) | Elog(%) | HRB | ||
| 304 | ≤0.08 | ≤0.75 | ≤2 | ≤0.045 | ≤0.030 | 8∽10 | 18∽20 | ≥205 | ≥520 | ≥40 | ≤90 | ||
| 301 | ≤0.15 | ≤1.00 | ≤2 | ≤0.045 | ≤0.030 | 6∽8 | 16∽18 | ≥205 | ≥515 | ≥40 | ≤95 | ||
| 316 | ≤0.08 | ≤1.00 | ≤2 | ≤0.045 | ≤0.030 | 10∽14 | 16∽18 | 2∽3 | ≥205 | ≥515 | ≥40 | ≤90 | |
| 316L | ≤0.03 | ≤1.00 | ≤2 | ≤0.045 | ≤0.030 | 12∽15 | 16∽18 | 2∽3 | ≥170 | ≥480 | ≥40 | ≤95 | |
| The specification of type 301,302,304,304L,309S,310S,316,316L,321,347 in conformity with ASTM & JIS criteria | |||||||||||||
| 400 series | |||||||||||||
| Grade | chemical composition (%) | mechanic performances | |||||||||||
| C | Si | Mn | P | S | Ni | Cr | Mo | Y.S(N/mm2) | T.S(N/mm2) | Elog(%) | HRB | ||
| 430 | ≤0.12 | ≤1.00 | ≤1 | ≤0.040 | ≤0.030 | 16∽18 | ≥450 | ≥205 | ≥22 | ≤88 | |||
| The specification of type 430,410,420J1.420J2 in conformity with ASTM & JIS criteria | |||||||||||||
| 630 series | |||||||||||||
| Grade | chemical composition (%) | mechanic performances | |||||||||||
| C | Si | Mn | P | S | Ni | Cr | Mo | Nb | Y.S(N/mm2) | T.S(N/mm2) | Elog(%) | HRB | |
| 630 | ≤0.07 | ≤1.00 | ≤1.00 | ≤0.035 | ≤0.030 | 6.50∽7.50 | 15.50∽17.50 | 0.15∽0.45 | ≥450 | ≥205 | ≥22 | ≤88 | |
| The specification of type 630 in conformity with ASTM & JIS standard | |||||||||||||
Stainless Steel Elements Content Table.pdf