DIN 2391 ST35 BK Thick Wall High - Precision Steel Tube , Round Cold Rolled Pipe
QuickDetail:
Description:
Standard:
ChinaStandardGB8162-2008,GB3639-2000
AmericanStandardASTMA106,ASTMA519,ASTMA513,ASTMA179
GermanyStandardDIN2391,DIN2445
JapaneseStandardJISG3445etc
European Standard EN10305
Specification
Designation | Symbol | Description |
Cold finished (hard) | BK(+C) | Tubes do not undergo heat treatment following the final cold forming and, thus, have a rather high resistance to deformation |
Cold finished (Soft) | BKW | The final heat treatment is followed by cold drawing involving limited deformation. Appropriate further processing allows a certain degree of cold forming (e.g. bending, expanding) |
Cold finished and stress-relieved | BKS(+SR) | Heat treatment is applied following the last cold forming process. Subject to appropriate processing conditions, the increase in the residual stresses involved enables both forming and machining to a certain degree. |
Annealed | GBK(+A) | The last Cold forming process is followed by annealing in a controlled atmosphere. |
Normalized | NBK(+N) | The last cold forming process is followed by annealing above the upper transformation point in a controlled atmosphere. |
DIN 2391 Precision seamless steel tube
This Standard applies to seamless precision steel tubes; and, in compliance with ISO/DIS 3304, those tube dimensions have een selectied from the range of manufactura le tu e dimensions which are mainly used as design elements
If tubes having the tolerances and are produced according to the technical conditions of deivery as specified in this Standard are to e used as pipelines, then the dimensions specified in DIN 2448 may from time to time be used. These tubes must be ordered according to quality grade C.
Grade | Mfg. Process | Chemical composition | |||||||||
C | Si | Mn | P | S | Ni | Cr | Mo | Others | ① | ||
② | |||||||||||
③ | |||||||||||
④ | |||||||||||
St30Si | S | 0.10Max | 0.30Max | ≤0.55 | 0.040Max | 0.040Max | - | - | - | - | ① |
② | |||||||||||
③ | |||||||||||
④ | |||||||||||
St30A1 | S | 0.10Max | 0.05Max | ≤0.55 | 0.040Max | 0.040Max | - | - | - | Al deoxydized | ① |
② | |||||||||||
③ | |||||||||||
④ | |||||||||||
St35 | S | 0.17Max | 0.35Max | ≥0.40 | 0.050Max | 0.050Max | - | - | - | - | ① |
② | |||||||||||
③ | |||||||||||
④ | |||||||||||
St45 | S | 0.21Max | 0.35Max | ≥0.40 | 0.050Max | 0.050Max | - | - | - | - | ① |
② | |||||||||||
③ | |||||||||||
④ | |||||||||||
St52 | S | 0.22Max | 0.55Max | ≥1.60 | 0.050Max | 0.050Max | - | - | - | - | ① |
② | |||||||||||
③ | |||||||||||
④ | |||||||||||
①Cold-finished/hard ②Cold-finished/soft ③Annealed ④Normalized
Grade | Material | Tensile Test MPa or N/mm2 | Remaks(Similar to JIS) | Possibility Temperature | |
Min Yield point | Tensile Strength | ||||
St30Si | 1.0211 | - | 400Min | (STKM11) | |
- | 355Min | ||||
- | 285Min | ||||
215 | 295~420 | ||||
St30Al | 1.0212 | - | 400Min | (STKM11) | |
- | 355Min | ||||
- | 285Min | ||||
215 | 295~420 | ||||
St35 | 1.0308 | - | 440Min | (STC38) | |
- | 370Min | ||||
- | 315Min | ||||
235 | 340~470 | ||||
St45 | 1.0408 | - | 540Min | (STKM13) | |
- | 470Min | ||||
- | 390Min | ||||
255 | 440~570 | ||||
St52 | 1.0580 | - | 590Min | (STKM19) | |
- | 540Min | ||||
- | 490Min | ||||
350 | 490~630 | ||||
Applications:
1. Automotive fields
A. Fuel injection lines/nozzles
B. CNG (Compressed Nature Gas) tube-- Burst pressure: 1307Bar,
Working Pressure: around 350bar
C. Drive transmission: Steering column elements
D. Gear shafts, hand brake, front axles, airbag inflators,
stabilizers, seat fasteners, front-wheel drive shafts
2. Hydraulic Fields
A. Hydraulic circuits (HPL), pneumatic lines, and hydraulic
suspension system
B. Hydraulic cylinders (HPZ)
Ouradvantage
Weownedspecialequipmentformanufacturingvarioushighprecisionproducts