Alu laminated metal plastic strip for optical fiber cable and communical cable
(1) Aluminum plastic composite belt should be continuous and tight composite, its surface should be smooth, smooth, uniform, no impurities, no wrinkles, no spots, and no other mechanical damage.
(2) the aluminum plastic composite belt should be tightly wound, and the belt should not be broken when used vertically.
(3) The side edge of the uncut aluminum plastic composite belt is allowed to have 2~5mm plastic film protection, and the side edge should be smooth, without coiling, notch, burr, etc
Defect, the misalignment between layers is not greater than 5mm.
(4) The cutting end face of the aluminum plastic composite belt should be flat, the roughness is less than 1mm, and there should be no roll edge, notch, knife mark, burr and other mechanical damage.When the composite tape is placed, it is not self-adhesive, and the edge should have no obvious wavy shape.
| Property | Unit | Values | Test Method | |
| Color | Natural or Blue | N/A | ||
| Thickness | AI | mm | 0.08-0.5 | N/A |
| EAA | mm | 0.05 | N/A | |
| Tensile Strength | MPa | ≥65 | ASTME8 | |
| Elongation at break | % | ≥20 | ASTME8 | |
| Peel strength | N/cm | ≥6.13 | ASTME B736 | |
| Heat Seal strength | N/cm | ≥17.5 | ASTME B736 | |
| Corrosion resistance (0.1 mol/L,Hcl,480h) | Grade | ≥7 | ﹍﹍﹍ | |
| Filler Resistance (68℃±1℃,168h) | ﹍﹍﹍ | No Delamination | PEA PE-39, PE-89 | |
| Peel strength after water bath (68℃±1℃, 168h) | N/cm | ≥6.13 | ASTME B736 | |
| Dielectric Strength (one side DC 1kv,1min, two sides DC 2kV,1min) | ﹍﹍﹍ | No Break | ﹍﹍﹍ |