1200mm Width AMS 5513 304L Annealed Precision Stainless Steel Strip For General Industry

304 Stainless Strip, Coil, Foil & Wire, AMS 5513, AMS 5910 (1/4H), AMS 5911 (1/2H), AMS 5912 (3/4H), AMS 5913 (FH), AMS 5501 (1/4H), ASTM A666

AMS 5513 304 Stainless steel strips coil Annealed No.1 2B Annealed For general industry  overview 

304L has oxidation resistance to a maximum temperature of 1650° F (899° C) continuously without appreciable scaling. The maximum temperature for intermittent exposure is 1500° F (816° C). Since 304L is an extra low-carbon variation of 304 it can often be used in the "as-welded" condition (without annealing), even in severe corrosive conditions, except for applications specifying stress relief. 304L has good welding characteristics and can be welded by all standard methods but attention needs to be paid to avoid weld "hot cracking". Welding may be followed by annealing to relieve stresses during severe forming or spinning.

PRODUCT FORMS:

Sheet, plate , Strip, pipe ,tube ,bar ,profiles

Equivalent Materials

AMS 5513 304 Stainless steel strips coil Annealed No.1 2B Annealed For general industry Products Specification and Dimension Ranges

Hot Rolled Strip Available Size

Width: 16.0~609.6 mm
Thickness: 2.5~10.0 mm
Available Steel Grade: 

Cold Rolled Strip Available Size

Width: 4.0~609.6 mm
Thickness: 0.1~3.0 mm

Surface Finish:

2B, 2D, BA, No.3, No.4, No.5, SB, HL, etc

Condition :

ANNEALED CONDITION

Ultimate Tensile Strength: 95 KSI min (655 MPA min) Yield Strength (0.2% Offset): 38 KSI min (260 MPA min) Elongation: 40%min Hardness: B95 max

TEMPERED 1/16 HARD

Ultimate Tensile Strength: 95 KSI min (655 MPA min) Yield Strength (0.2% Offset): 45 KSI min (310 MPA min) Elongation: 40% min

Tempered 1/8 Hard Ultimate Tensile Strength: 100 KSI min (690 MPA min) Yield Strength (0.2% Offset): 55 KSI min (380 MPA min) Elongation: 45% min

TEMPERED 1/4 HARD

Ultimate Tensile Strength: 125 KSI min (860 MPA min) Yield Strength (0.2% Offset): 75 KSI min (515 MPA min) Elongation: 25% min

TEMPERED 1/2 HARD

Ultimate Tensile Strength: 150 KSI min (1035 MPA min) Yield Strength (0.2% Offset): 110 KSI min (760 MPA min) Elongation: 15% < 0.15" 18% > 0.15"

TEMPERED 3/4 HARD

Ultimate Tensile Strength: 175 KSI min (1205 MPA min) Yield Strength (0.2% Offset): 135 KSI min (930 MPA min) Elongation: 10% < 0.15" 12% > 0.15"

TEMPERED FULL HARD

Ultimate Tensile Strength: 185 KSI min (1275 MPA min) Yield Strength (0.2% Offset): 140 KSI min (965 MPA min) Elongation: 8% < 0.15" 9% > 0.15"

Available Steel Grade:

Stainless steel : Type 201, 202, 205, 301, 302, 302B, 303, 303Se, 304, 304L, 302HQ, 304N, 305, 308, 309, 309S, 310, 310S, 314, 316, 316L, 316F, 316N, 317, 317L, 317LMN, 321, 330, 347, 348, 384, 405, 409, 429, 430, 430F, 430FSe, 434, 436, 442, 446, 403, 410, 414, 416, 416Se, 420, 420F, 422, 431, 440A, 440B, 440C,  630 ,  13-8 PH ,15-5 PH , 17-7 PH ,17-4 ph , 904L , A286 ,VG-10 ,  SAE 316 , SAE 316L , SAE 440 ,  SAE 420

Duplex stainless steel : 2205 , 2304 , 2507 

Nickel alloy :  

Titanium and titanium alloys  

AMS 5513 304 Stainless steel strips coil Annealed No.1 2B Annealed For general industry  Application 

APPLICATIONS

Medical Parts Manufacturing
Manufacture of Surgical Parts
Tubing
Flexible Metal Hose
Bellows

AMS 5513 304 Stainless steel strips coil Annealed No.1 2B Annealed For general industry  Technical datasheet

ADDITIONAL PROPERTIES

FINISHES

# 1 - Hot rolled annealed and descaled. It is available in strip, foil and ribbon. It is used for applications where a smooth decorative finish is not required.

# 2D - Dull finish produced by cold rolling, annealing and descaling. Used for deep drawn parts and those parts that need to retain lubricants in the forming process.

# 2B - Smooth finish produced by cold rolling, annealing and descaling. A light cold rolling pass is added after anneal with polished rolls giving it a brighter finish than 2D. #BA- Bright annealed cold rolled and bright annealed #CBA- Course bright annealed cold rolled matte finish and bright anneal

#2 - Cold Rolled

# 2BA- Smooth finish produced by cold rolling and bright annealing. A light pass using highly polished rolls produces a glossy finish.

2BA finish may be used for lightly formed applications where a glossy finish is desired in the formed part. Polished - Various grit finish for specific polish finished requirements. * Special finishes are available for all alloys - Contact US for more information

.

AMS 5513 304 Stainless steel strips coil Annealed No.1 2B Annealed For general industry Products display and Package Details 

FAQ

Q: Would you provide samples For free?

A: Yes . with on stock specification We provide samples For Free . Freight charge collect