304L stainless steel is a versatile stainless steel material, which is widely used in the manufacture of equipment and parts requiring good comprehensive properties (corrosion resistance and formability).Also known as ultra low carbon stainless steel
Coil , Sheet, plate , Strip, pipe ,tube ,bar ,profiles
Equivalent Materials<These Info is just for refrenence .>
| AISI 316L equivalents | |||
| ASTM A182 Grade F316L | ASTM A955 Grade S31603 | JIS SCS16A | |
| ASTM A182 Grade F316LN | ASTM A959 Grade S31603 | EN GX2CrNiMo19-11-2 | |
| ASTM A193 Grade B8MLN Class 1 | ASTM A959 Grade S31653 | EN 1.4409 | |
| ASTM A193 Grade B8MLN Class 1D | ASTM A959 Grade S31654 | UNS J92800 | |
| ASTM A193 Grade B8MLNA Class 1A | ASTM A965 Grade F316LN | DIN 1.4432 | |
| ASTM A194 Grade 8MLN | ASTM A988 Grade S31603 | AFNOR Z3CND17-12-03 | |
| ASTM A194 Grade 8MLNA | ASTM A988 Grade 18Cr8Ni | BS 316S13 | |
| ASTM A240 Grade S31603 | ASTM A988 Grade S31653 | JIS SUS316LFB | |
| ASTM A240 Grade S31653 | ASTM A988 Grade 18Cr8Ni with Mo and N | JIS SUSF316L | |
| ASTM A249 Grade TP316L | ASTM F2281 Grade S31603 | EN X2CrNiMo17-12-3 | |
| ASTM A249 Grade TP316LN | ASTM F2281 Type I Class A | EN 1.4432 | |
| ASTM A276 Grade S31603 | ASTM F593 Grade S31603 | GOST 06Ch17N13M3-WD | |
| ASTM A276 Grade S31653 | ASTM F593 Grade Alloy Group 2 | DIN 1.4435 | |
| ASTM A276 Grade S31654 | ASTM F594 Grade S31603 | DIN X2CrNiMo18-14-3 | |
| ASTM A314 Grade S31603 | ASTM F594 Alloy Group 2 | AFNOR Z3CND18-14-03 | |
| ASTM A320 Grade B8MLN Class 1 | ASTM F738M Grade S31603 | BS 316S11 | |
| ASTM A320 Grade B8MLNA Class 1A | ASTM F738M Grade Alloy Group A4 | BS 316S31 | |
| ASTM A336 Grade F316LN | ASTM F836M Grade S31603 | SS 2353 | |
| ASTM A358 Grade A240 Type 316 | ASTM F836M Grade Alloy Group A4 | UNE X2CrNiMo18-14-3 | |
| ASTM A358 Grade 316 | ASTM F837 Grade S31603 | AISI 316LMo | |
| ASTM A358 Grade A240 Type 316L | ASTM F837 Grade Property Class A1 | SAE 316LMo | |
| ASTM A358 Grade A240 Type 316LN | ASTM F879 Grade S31603 | JIS SUS316LTBS | |
| ASTM A403 Grade CR316L | DIN 1.4404 | JIS SUS316LTP | |
| ASTM A403 Grade 316L | DIN X2CrNiMo18-10 | JIS SUS316LTPY | |
| ASTM A403 Grade CR316LN | DIN X2CrNiMo17-12-2 | JIS SUS316LTB | |
| ASTM A403 Grade WP316L | DIN G-X2CrNiMoN18-14 | JIS SUSY316L | |
| ASTM A403 Grade WP316LN | DIN GX2CrNiMoN18-14 | JIS SUS316J1L | |
| ASTM A473 Grade 316L | DIN X2CrNiMoN17-12-2 | JIS SUSY316J1L | |
| ASTM A478 Grade 316L | DIN X2CrNiMo17-13-2 | EN X2CrNiMo18-14-3 | |
| ASTM A479 Grade S31603 | DIN G-X2CrNiMoN18-10 | EN 1.4435 | |
| ASTM A479 Grade S31653 | AFNOR Z2CND17-12 | GOST 03Ch17N14M3 | |
| ASTM A493 Grade S31603 | BS 316S12 | GB 00Cr18Ni15Mo3 | |
| ASTM A580 Grade S31603 | UNI X2CrNiMo1712 | DIN 1.4409 | |
| ASTM A632 Grade TP316L | SS 2343 | BS 316C12 | |
| ASTM A666 Grade S31603 | SS 2348 | ||
| ASTM A774 Grade TP316L | SS 2553 | ||
| ASTM A778 Grade TP316L | SAE 316L | ||
| ASTM A793-96 Grade 316L | JIS SUS316L | ||
| ASTM A813 Grade TP316L | JIS SCS16 | ||
| ASTM A813 Grade TP316LN | EN X2CrNiMo17-12-2 | ||
| ASTM A814 Grade TP316L | EN 1.4404 | ||
| ASTM A814 Grade TP316LN | GOST 03Ch17N13M2 | ||
| ASTM A943 Grade TP316L | GB 022Cr17Ni12Mo2 | ||
| ASTM A943 Grade TP316LN | UNS S31603 | ||
| AISI 316 equivalents | ||
| ASTM A193 Grade B8M Class 1 | ASTM A666 Grade S31600 | JIS SUSF316 |
| ASTM A193 Grade B8M Class 1D | ASTM A688 Grade TP316 | JIS SUS316TKC |
| ASTM A193 Grade BSM Class 2 | ASTM A813 Grade TP316 | JIS SUS316TP |
| ASTM A193 Grade B8M2 Class 2B | ASTM A814 Grade TP316 | JIS SUS316TB |
| ASTM A193 Grade B8M3 Class 2C | ASTM A943 Grade TP316 | JIS SUS316TBS |
| ASTM A193 Grade B8MA Class 1A | ASTM A959 Grade S31600 | JIS SUS316TPY |
| ASTM A194 Grade 8M | ASTM A965 Grade F316 | JIS SUS316TPD |
| ASTM A194 Grade 8MA | ASTM F2281 Grade S31600 | JIS SUS316HTP |
| ASTM A213 Grade TP316 | ASTM F2281 Type I Class A | JIS SUS316HTB |
| ASTM A249 Grade TP316 | ASTM F593 Grade S31G00 | JIS SUS316HTF |
| ASTM A269 Grade TP316 | ASTM F593 Grade Alloy Group 2 | JIS SUS316F |
| ASTM A269 Grade 316 | ASTM F594 Grade S31600 | EN X5CrNiMo17-12-2 |
| ASTM A270 Grade TP316 | ASTM F594 Grade Alloy Group 2 | EN 1.4401 |
| ASTM A276 Grade S31600 | ASTM F738M Grade S31600 | ISO A4 |
| ASTM A3121 Grade TP316 | ASTM F738M Grade Alloy Group A4 | GOST 0Cr17Ni12Mo2 |
| ASTM A3121 Grade 316 | ASTM F836M Grade S31600 | GB 08Ch27N13M2 |
| ASTM A314 Grade S31635 | ASTM F836M Grade Alloy Group A4 | UNS S31600 |
| ASTM A314 Grade S31640 | ASTM F837 Grade S31600 | DIN 1.4436 |
| ASTM A320 Grade B8M Class 1 | ASTM F837 Grade Property Class A1 | DIN X5CrNiMo17-13-3 |
| ASTM A320 Grade 316 | ASTM F879 Grade S31600 | DIN X3CrNiMo17-13-3 |
| ASTM A320 Grade B8M Class 2 | DIN 1.4401 | AFNOR Z7CND18-12-03 |
| ASTM A320 Grade B8MA Class 1A | DIN 316S42 | BS 316S13 |
| ASTM A336 Grade F316 | DIN 316S33 | UNI X8CrNiMo1713 |
| ASTM A376 Grade TP316 | DIN X5CrNiMo17-12-2 | SS 2343 |
| ASTM A376 Grade 316 | DIN X 5 CrNiMo 18 10 | JIS SCS14 |
| ASTM A403 Grade CR316 | AFNOR Z7CND17-11-02 | EN X3CrNiMo17-13-3 |
| ASTM A403 Grade 316 | BS 316S16 | EN 1.4436 |
| ASTM A403 Grade WP316 | UNI X5CrNiMo1712 | ISO A5 |
| ASTM A409 Grade TP316 | SS 2347 | DIN 1.4984 |
| ASTM A409 Grade 316 | UNE F.3543 | AFNOR 9165-041 |
| ASTM A479 Grade S31600 | SAE 316 | AFNOR 9165 25 |
| ASTM A511 Grade MT316 | JIS SUS316 | AFNOR Z 10 CNW 17 |
| ASTM A554 Grade MT316 | JIS SUS316TKA | EN 1.4984 |
| ASTM A632 Grade TP316 | JIS SUS316TF | JIS SUS316FB |
| 316 Stainless Steel Coil Specification | ASTM A240 / ASME SA240 AMS 5524 5507 |
| 316 Stainless Steel Coil Manufacturing Process | Hot Rolled (HR) / Cold Rolled (CR) |
| 316 Stainless Steel Coil Grades | 202 / 304 / 304L / 304H / 309S / 310S / 316 / 316L / 316Ti / 317L /
321 / 321H / 347 / 347H / 904L etc. UNS No. - UNS S30400, UNS S30403, UNS S31008, UNS S31620, UNS S31603, UNS S31603, UNS S31635, UNS S31703, UNS S32100, UNS S34700, UNS S34709, UNS S8904 EN No. - 1.4301, 1.4307, 1.4845, 1.4401, 1.4404, 1.4571, 1.4438, 1.4541, 1.4550, 1.4551, 1.4539 |
| 316 Stainless Steel Coil Thickness | 0.6 MM TO 80 MM THICKNESS |
| 316 Stainless Steel Coil Width | 1250 MM / 1500 MM / 2000 MM / 04 Feet / 05 Feet and Custom Cut Width as Per Requirement |
| 316 Stainless Steel Coil Length | 2400 MM / 2420 MM / 6000 MM / 08 Feet / 10 Feet / Coil Cut and Custom Cut Length as Per Requirement |
| 316 Stainless Steel Coil Surface Finish | 2B, 2D, BA, MATT, MATT PVC, No.4, No.5, SB, HR, No.8, Mirror, Hairline, Brush, Textured, Oil base wet Polished, Both sides Polished available. |
| 316 Stainless Steel Coil Protective and Coating | Paper Interleaved or Vinyl Masked, PVC coating Normal / Laser, Film: 100 micrometer, Color: black/white. |
| 316 Stainless Steel Coil Value Added Services | Gas Cutting / CNC Plasma Cutting / Profiling / Rolling / Bending / Coil Metal Fabrication / Drill / Punch / Machining / Sand Blasting / Shot Blasting / Heat Treatment |
| 316 Stainless Steel Coil Packaging | steel sheet and steel angles and protective wood frame and paper |
Dimension Ranges:
Width | Thickness | Inner Diameter | Steel Grade | Surface Finish |
| 610~2030 mm | 0.15~3.0 mm | 610 or 508 +0/-5 mm | 201; 254 SMO; 301; 301 AL; 301Si; 302; 303; 303 SE; 304; 304 L; 304 LV; 304 V; 3049; 305;30512; 308; 309; 309 S; 309 SCB; 310; 310 S; 316; 316 L; 316 LN; 316 Ti; 317; 317 L; 321; 330; 347; 384; 405; 409; 410; 410 S; 414;416; 416 SE; 420; 420 A; 420 HC; 420 LC; 420 MO; 430; 430Li; 434; 436; 439; 440 A; 440 C; 441; 442; 444; 446; 18 SR1;Carpenter 20,CB32; Carpenter 4552; Custom 450; 18-9LW1; 19-90L4; Greek Ascology;; AL-6XN4; 904L; Duplex 2205; Duplex 2304; Duplex 2507,Nickel alloys , Titanium and Ti alloys | 2B, 2D, BA, No.3, No.4, No.5, SB, HL |
| 610~2030 mm | 2.5mm~10 mm | 610 or 508 +0/-5 mm | No.1 or As requied |
Striping processing, commonly known as “slitting “, refers to the winding of a metal coil by unwinding, slitting, leveling, winding, and processing into a desired width. Slitting processing is a basic metal processing technology that combines high-quality equipment with skilled craftsmanship. it can be obtained with strict tolerance, perfect surface control , safe packaging as well as fine transportation.
CHEMICAL COMPOSITION: ASTM A240, A666
| Element | Type 316 | Type 316L |
|---|---|---|
| Carbon | 0.08 max. | 0.030 max. |
| Manganese | 2.00 max. | 2.00 max. |
| Sulfur | 0.030 max. | 0.030 max. |
| Phosphorus | 0.045 max. | 0.045 max. |
| Silicon | 0.75 max. | 0.75 max. |
| Chromium | 16.0 – 18.0 | 16.0 – 18.0 |
| Nickel | 10.00 – 14.00 | 10.00 – 14.00 |
| Molybdenum | 2.00 – 3.00 | 2.00 – 3.00 |
| Nitrogen | 0.10 max. | 0.10 max. |
| Type | Yield Strength 0.2% offset (KSI) | Tensile Strength (KSI) | % Elongation (2″ Gauge length) |
|---|---|---|---|
| 316 | 30 min. | 75 min. | 40 min. |
| 316L | 25 min. | 70 min. | 40 min. |
| Density (lb./ in^2) @ RT | 0.29 | |
|---|---|---|
| Modulus of Elasticity in Tension (psi x 10^6) | 28.0 | |
| Specific Heat (BTU/o F/lb.) | 32 to 212 oF | 0.12 |
| Thermal Conductivity (BTU/hr/ft^2/ft) | 212oF | 9.4 |
| 932oF | 12.4 | |
| Mean Coefficient of Thermal Expansion (in. x 10^-6 per o F) | 32 to 212oF | 8.9 |
| 32 to 600oF | 9.0 | |
| 32 to 1,000oF | 9.7 | |
| 32 to 1,200oF | 10.3 | |
| Electrical Resistivity (micro ohms – cm) | at 70oF | 29.4 |
| Melting Point Range (oF) | 2500 – 2550 |
PROCESSING:
Types 316 and 316L are non-hardenable by heat treatment. Annealing: Heat to 1900 – 2100°F then rapidly quench Forming: Types 316 and 316L can be readily formed and drawn.
These alloys are generally considered to have poorer weldability than Types 304 and 304L. A major difference is the higher nickel content for these alloys which requires slower arc welding speed and more care to avoid hot cracking. When filler is needed, AWS E/ER 316L and 16-8-2 are most often specified.
Types 316 and 316L Stainless Steels exhibit better corrosion resistance than Type 304. They provide excellent pitting resistance and good resistance to most chemicals involved in the paper, textile and photographic industries.
FAQ
Q: Would you provide samples For free?
A: Yes . with on stock specification We provide samples For Free . Freight charge collect
Q: What information should i provide to source for the right products ?
A: Material grade, width, thickness, coating and Purchase quantity , Expected lead time ,etc
Q: What are the shipping ports?
A:Under normal circumstances, we ship from Shanghai, Tianjin, Qingdao, Ningbo ports, you
can choose other ports according to your needs.
Q: About product prices?
A:Prices vary from period to period due to cyclical changes in the price of raw materials.
Q: How long does your delivery time take?
A:In general, our delivery time is within 5-45 days, and may be delayed if the demand is extremely
large or special circumstances occur.
Q: Can I visit your location?
A: Of course, we welcome customers from all over the world to visit our factory. However, some
of the plants are not open to the public.
Q: Does the product have quality inspection before loading?
A: Of course, all our products are strictly tested for quality before packaging, and unqualified
products will be destroyed.
Q: How to pack the products?
A:The inner layer has a waterproof paper outer layer with iron packaging and is fixed with a fumigation
wooden pallet. It can effectively protect products from corrosion during ocean transportation.
Q: What is your working time?
A: In general, our online service time is Beijing time: 8:00-22:00, after 22:00,
we will reply to your inquiry during the next working day.