Aluminium Oxide, Al2O3 is the most widely applied and cost effective technical ceramic material. It offers a combination of superior mechanical strength and electrical properties, wear resistance and corrosion resistance. The maximum working temperature is up to 1700 °C with relatively high thermal conductivity. It is also an electrically insulating material with a high electrical resistivity. The good corrosion resistance makes it insoluble in water and slightly soluble in strong acid and alkaline solution.
KAMTAI manufactures and provides alumina ceramic components for a wide range of application like Mechanical Equipment, Electronic & Electrical, Oil Drilling, Medical, Chemical Industry etc. According to actual application and customer's requirement, the purities vary from 95%-99.7% and the forming methods will be different. The forming methods applied in our plant include dry pressing, isostatic pressing, injection moulding, extrusion moulding. With experienced engineers and talented workers, we are confident to offer high quality, high precision, complex components for customers worldwide.
Other information:
| Feature | Application | Main usage |
| 1.Great mechanical strength | Electric appliance industry Automotive industry | 1.Heat treatment furnace and toughened furnace |
| 2.High softening temperature | ||
| 3.Good resistance to thermal impact | ||
| 4.Small thermal expansion coefficient | Mechanical industry Engineer industry | 2.Inner liner tube and heating tube in electric furnace |
| 5.Good chill and abrupt heat properties | ||
| 6. Resistance to acid and alkali corrosion |
MATERIAL PROPERTIES
| Unit | 95% Al2O3 | 99% Al2O3 | ZrO2 | GP-Si3N4 | |
| Color | - | white | ivory | white | gray |
| Density | g/cm³ | 3.65 | 3.88 | 5.95 | 3.22 |
| Water Absorption | % | 0 | 0 | 0 | 0 |
| Young's Modulus | Gpa | 280 | 350 | 205 | 295 |
| Vickers Hardness | Gpa | 14 | 20 | 12 | 18-20 |
| Flexural Strength ( at R.T. ) | Mpa | 280 | 300 | 900 | 650 |
| Compressive Strength ( at R.T. ) | Mpa | 2000 | 2500 | 2200 | 2200 |
| Thermal Conductivity ( at R.T. ) | W/(m.K) | 18-25 | 30 | 2.2 | 25 |
| Thermal Shock Resistance | ΔT(°C) | 220 | 180-200 | 280-350 | 450-650 |
| Max. Working Temperature ( at R.T. ) | °C | 1500 | 1700 | 850 | 1200 |
| Volume Resistivity ( at R.T. ) | Ω.cm | >10^15 | >10^14 | >10^12 | >10^14 |
| Dielectric Constant (1 MHz at R.T. ) | - | 9.50 | 9.80 | 26 | 8.20 |
| Dielectric Strength | kV/mm | 16 | 22 | - | 16 |