88A 1.45G/Cm3 Cable Insulation Flame Retardant PVC Compound Cable Sheathing
| Specs | Features | Application |
Component Wire Material | Passed UL test, Cold-form test -20 ℃, Heat resistance grade: 60℃ 75℃ 90℃ 105℃, Combustion test: VW-1 FT2, Environment friendly. |
component wire material. |
Component Wire Material |
60℃ 75℃ 90℃ 105℃, Combustion test: VW-1 FT2, Environment friendly. |
wire material |
1.Technical specifications of 70 ℃ pvc compound
| Tensile strength | MPa | 20.5 |
| Fracture tensile strain | % | 320 |
| Ageing temperature | ℃ | 100 |
| Ageing time | h | 168 |
| Tensile strength after ageing | MPa | 22.5 |
| Max change of tensile strength | % | +12 |
| After ageing fracture tensile strain | % | 290 |
| Max change of fracture tensile strain | % | -10 |
| Thermal deformation | % | 28 |
| Thermal ageing quality loss | g/m2 | 19 |
| 200℃ thermal stability time | min | 90 |
| 20℃ volume resistivity | Ω.cm | 2.0*1011 |
Technical specifications of 90 ℃ pvc resin compound
| Tensile strength | MPa | 20 |
| Fracture tensile strain | % | 330 |
| Ageing temperature | ℃ | 100 |
| Ageing time | h | 240 |
| Tensile strength after ageing | MPa | 21.5 |
| Max change of tensile strength | % | +8 |
| After ageing fracture tensile strain | % | 310 |
| Max change of fracture tensile strain | % | -6 |
| Thermal deformation | % | 28 |
| Thermal ageing quality loss | g/m2 | 9 |
| 200℃ thermal stability time | min | 120 |
| 20℃ volume resistivity | Ω.cm | 2.0*1010 |
2,Use and standard: wire and cable
3,Process: extrusion
4,Appearance: cylindrical particles, plastication should be good, the color and luster is even, without obvious impurity.
5,color: Any colors, base on requirement.
6,Packing: 25kg net weight per in a kraft bag.
7, Transportation and storage:
This kind of product in the transportation should not be weathered, should be stored in a clean, cool, dry and ventilated warehouse , storage period is from the date for a year.
We will also produce the products according with customer's requirement, For example, Flame-resisting compounds, Low temperature resisting compounds, Heat-resistant compounds, and low smoke low halogen compounds, Transparent PVC compounds etc.
black colors wire and Power Cable PVC compound pictures