Haynes 282 Nickel Alloy for High Temperature Structural Applications
HAYNES 282 is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and land-based gas turbine engines. It possesses a unique combination of creep strength, thermal stability, weldability, and fabricability. The alloy has excellent creep strength in the temperature range of 1200 to 1700°F (649 to 927°C), surpassing that of Waspaloy alloy, and approaching that of R-41 alloy.
Easily Fabricated
This high level of creep strength in HAYNES 282 alloy has been
attained at a relatively low volume fraction of the strengthening
gamma-prime phase, resulting in outstanding resistance to
strain-age cracking (normally a problem with superalloys in this
creep strength range). Additionally, slow gamma-prime precipitation
kinetics allow for the alloy to have excellent ductility in the
as-annealed condition. Consequently, HAYNES 282 exhibits superior
weldability and fabricability.
Heat Treatment
HAYNES 282 alloy is provided in the solution-annealed condition, in which it
is readily formable.
The typical solution-annealing temperature is in the range of 2050
to 2100°F (1121 to 1149°C). After component fabrication, a two-step
age hardening treatment is required to put the alloy into the
high-strength condition. The treatment includes 1850°F (1010°C) / 2
hours / AC (air cool) + 1450°F
(788°C) / 8 hours / AC.
Chemical composition
Element | C | Mn | Si | P | S | Cr | Co | Mo | Ti |
Weight(%) | 0.04~0.08 | 0.3 max | 0.15 max | 0.015 max | 0.015 max | 18.5~20.5 | 9.0~11.0 | 8.0~9.0 | 1.9~2.3 |
Element | Al | Zr | B | Fe | Cu | Ni | Ta | Nb | W |
Weight(%) | 1.38~1.65 | 0.02 max | 0.003~0.010 | 1.5 max | 0.1 max | Rem | 0.1 max | 0.2 max | 0.5 max |
Applications
The features of HAYNES 282 alloy make it suitable for
critical gas turbine applications, such as
sheet fabrications, seamless and flash butt-welded rings, and cases
found in compressor, combustor, and turbine sections. In augmented
aircraft gas turbines, the new alloy will be useful for
exhaust and nozzle components. In industrial gas turbines,
HAYNES 282 alloy is a good candidate for transition sections
and other hot-gas-path components.
Forms of supply
Round bar
Forging
Sheet
Strip
Pipe