TC21 titanium alloy bars stock
Baoji Lihua Non-ferrous Metals Co., Ltd, founded in 2006, lies in Tai Cheng road Baoji city---It is famous for manufacturing titanium, called “China Titanium Valley”.
TC21, titanium alloy is a new type of titanium alloy with high strength, high toughness and high damage tolerance developed by the Northwest Nonferrous Metals Research Institute. It belongs to the Ti-Al-Sn-Zr-Mo-Cr-Nb(-Ni-Si) series Two-phase titanium alloy has good strength, plasticity, fracture toughness and low crack growth rate.
Product Description
Product name | TC21 titanium alloy bars stock |
| Standard | GB/T2965-2007,JIS H4650-2001,ASTM B348-06,DIN17862-93, ASTM F136,AMS4928,GB/T13810,Q/BS5331-91,etc |
| Grade | TC21 |
| Surface Treatment | polished, bright finish etc. |
| Feature | 1. Low Density and High Strength 2. Excellent Corrosion Resistance 3. High ballistic resistance-to-density ratio. 4. Excellent Bearing to cryogenic property |
| Packaging | Wooden case or as per client requirement |
| MOQ | 10KG |
| Leadtime | Within 15 days |
Advantage is introduced
| Low Density and High Strength | The density is low, the specific strength of titanium is 4.51g/cm3, higher than aluminum, lower than steel, copper, nickel, but its strength is at the top of the metal |
| Excellent Corrosion Resistance | Special Erosion -corrosion reslstance. In the medulla containing oxygen, a dense, solid binder and inert oxide film are formed on the surface of titanium to protect the corrosion of titanium matrix |
| High ballistic resistance-to-density ratio. | The vibration attenuation time of titanium metal is longer than that of steel and copper metal after mechanical and electrical vibration |
| The tensile strength is close to its yield strength | Due to the large field limit and elastic modulus of titanium, the resilience of titanium in the forming process is large |
| TC21 | ||||
| Chemical compositions(weight%,<=) | ||||
| Ti | Al | Sn | Zr | Mo |
| Remain | 6.2 | 2.1 | 1.7 | 3.0 |
| Cr | Nb | Fe | Si | Other |
| 1.7 | 1.9 | 0.09 | 0.1 | 0.5 |
| Physical properties(>=) | ||||
Σb Tensile Strength (Mpa) | σr0.2 Yield Strength (Mpa) | δL0+50mm Elongation (%) |
ψ Elongation (%) | |
| 1140 | 1010 | 13 | 25 | |
Titanium bar UT test (Ultrasonic Testing )
Professional third-party testing
7. Cooperation with us will provide you a strong guarantee:
1.ISO9001:2015
2. The timely delivery rate is 99.8%, sometimes in advance.
3.Excellent after-sale service.
4.Rapid inquiry reply, within 2 hours.
5.Fair payment term
6.Professional technical adviser
7.Material certificate
8.Quality is strictly according to ASTM,DIN,UNS,GB/T
standard(manufacturing process,surface treatment,inspections and
testing).