High Quality TA1 TA2 TC4 Titanium Bar Titanium Rod Price Per Kg Customized Surface
TA18 titanium alloy is an advanced α-type titanium alloy with a
nominal composition of Ti-3A12V. It was developed as a cold
processable pipe material. At room temperature and high
At temperature, its strength is 209% -50% higher than pure
titanium, and its welding performance and cold forming performance
are better than TC4 alloy. The maximum operating temperature is
about 315 ° C. Although the strength of this alloy is not as high
as that of TC4 alloy, it has been widely used because of its
excellent cold workability.
Product Description
Product name | TA18 Ti 3Al2.5V Alloy Grade 9 Titanium Bar |
Standard | ASTMB348/ASTM F67/ASTM F136 |
Material | Pure titanium and titanium alloys |
Advantages | 1. Resistance to acid and alkali corrosion, seawater corrosion and sewage corrosion 2. Low density, light weight 3. The non-magnetic 4. When used between -253-600°, its tensile strength is almost the highest among metals |
Chemical compositions(weight%,<=) | ||||||||
Main component | other | |||||||
Ti | V | Fe | C | N | H | O | single | total |
Remain | 1.5-3.0 | 0.25 | 0.08 | 0.05 | 0.015 | 0.12 | 0.10 | 0.30 |
Physical properties(>=) | ||||||
alloy composition | Σb Tensile Strength (Mpa) | σr0.2 Yield Strength (Mpa) |
ψ Elongation (%) | |||
Ti 3Al2.5V | Ksi | Mpa | Ksi | Mpa | 15F | |
90 | 620 | 1010 | 13 |