Changshu Longteng Special Steel Co., Ltd. |
|
ER70S-4 MIG Welding Wire Carbon Steel MIG Wire
Specification:
ER70S-4 is a silicon and manganese deoxidized wire used for mild and low alloy steel general purpose fabrication. A well balanced silicon and
manganese content permits its use with CO2, Argon-Oxygen mixtures, or mixtures of the two. This wire may be used for short-circuiting arc (dip-transfer), buried arc, as well as spray transfer arc processes. ER70S-4 produces quality welds with rimmed steels, better welds on semi-killed
steels and excellent welds on killed steels. It yields an almost slag-free deposit which does not require cleaning for many applications thereby
providing low plate preparation costs, good bead appearance and welder satisfaction.
Applications:
Automobile frames, earthmoving and farm equipment, sheet metal, ships and barges, railcars, trailers, ornamental iron, metal furniture, storage bins and general fabrications.
Chemical Composition(%)
Chemical Composition | C | Mn | Si | S | P | Ni | Cr | Mo | V | Cu |
Guarantee Value | 0.06~0.15 | 1.00~1.50 | 0.65~0.85 | ≤0.025 | ≤0.025 | ≤0.15 | ≤0.15 | ≤0.15 | ≤0.03 | ≤0.50 |
General Result | 0.085 | 1.05 | 0.718 | 0.014 | 0.014 | 0.005 | 0.018 | 0.006 | 0.003 | 0.106 |
Mechanical Properties of Deposited Metal
Test Item | Rm(MPa) | ReL/Rp0.2(MPa) | A(%) | KV2(J) -30℃ |
Guarantee Value | ≥500 | ≥420 | ≥22 | No requirements |
General Result | 540 | 450 | 30 | 93,87,95 |
Reference Current(DC+)
Size(mm) | Current range (A) | GAS flow rate(L/min) |
Φ0.8 | 50~100 | 15 |
Φ1.0 | 50~220 | 15~20 |
Φ1.2 | 80~350 | 15~25 |
Φ1.6 | 170~550 | 20~25 |