E71T-C1A4-Ni1 Flux Cored Arc Welding Wire 2/11/33/44 lb
LT·E501Ni
Conform to Standard :GB/T 17493 E491T1-Ni1C
AWS A5.36 E71T1-C1A4-Ni1, JIS Z3313 T493T1-1CA-N2
ISO 17632-B-T493T1-1CA-N2
Specification:
E71T1-C1A4-Ni1 is an all-position, flux cored welding wire intended for single and multiple pass welding of low-alloy and carbon steel where a minimum 70 kpsi tensile strength and good notch toughness is required. It is an excellent general purpose welding wire
Purpose:
Most widely used for welding some key structures like shipbuilding, mechanical manufacture, pressure vessels, boilers, petroleum machinery, chemical machinery, hoisting machinery etc.
Chemical Composition(%)(Shielding Gas:CO2)
| Chemical Composition | C | Mn | Si | S | P | Ni | Cr | Mo | V |
| Guarantee Value | ≤ 0.12 | ≤ 1.50 | ≤ 0.80 | ≤0.030 | ≤0.030 | 0.80~ 1.10 | ≤ 0.15 | ≤ 0.35 | ≤ 0.05 |
| General Result | 0.04 | 1.28 | 0.38 | 0.006 | 0.011 | 0.90 | - | - | - |
Mechanical Properties of Deposited Metal(Shielding Gas:CO2)
| Test Item | Rm(MPa) | ReL/Rp0.2(MPa) | A(%) | KV2(J) -30℃ -40℃ | |
| Guarantee Value | 490~620 | ≥400 | ≥20 | ≥27 | - |
| General Result | 570 | 510 | 27 | 135 | 120 |
Diffusion hydrogen content of the deposited metal (Mercury Method)≤10ml/100g
Reference Current(DC+)
| Size(mm) | Φ1.2 | Φ1.4 | Φ1.6 | |
| Current Range (A) | Flat Position | 120~300 | 150~400 | 180~450 |
| Vertical Upward welding/ Overhead position | 120~260 | 150~270 | 180~280 | |
| Vertical Downward weldingOverhead position | 200~300 | 220~300 | 250~300 | |
| Horizontal Welding | 120~280 | 150~320 | 180~350 | |
Notes:
1.Adopt degreasing and rust cleaning process before operate.
2.Shielding gas flow: 20-25L/min when welding
3.Extension: 15-25mm
4.The humidity of welding wire storage should be less than 60%
5.Storage period: Vacuum packaging less than 1 Year, other packaging less than half year.