SHANGHAI COMMON METAL PRODUCTS CO., LTD |
|
6000 Series 8kg/M T Slot Flat Anodizing Aluminum Profile
Auminium as most of metals, requires heat treatments to obtain the desired mechanical properties. For aluminium, as to nickel or titanium, the hardening process is by aging. For this reason is important define the heat treatment according to the application. The three more common heat treatments applied to aluminium profiles are:
T4: Tempered from the solution temperature by forced air, natural
aging.
T5: Tempering treatment from the extrusion temperature using forced
air, then artificial aging. It is the most common heat treatment on
aluminum profiles to doors and windows profiles.
T6: Tempered from the solution temperature by water (under 40ºC)
and artificial aging.
Material | 6063-T5 aluminum alloy |
Standard | European Standard |
Alloy or not | Alloy |
Size | 20mm*20mm |
Surface treatment | Anodized |
Hardness | 62HB |
Tensile Strength | 180Mpa |
Yield Strength | 127Mpa |
Elasticities Modulus | 68600N/mm |
Elongation | 8% |
SURFACE TREATMENTS
The followings are the most common surface treatments of our
aluminum profiles, to allow our customers satisfaction for any
constructive necessity.