AISI 310MoLN stainless steel is an alloy of iron, further classified as an austenitic stainless steel. It is typically furnished in the solution annealed (AT) condition. 310MoLN is the AISI designation for this material. 1.4466 is the EN numeric designation. S31050 is the UNS number. Additionally, the EN chemical designation is X1CrNiMoN25-22-2.
Base Metal Price46 % rel
Density7.9 g/cm3 (490 lb/ft3)
Elastic (Young's, Tensile) Modulus200 GPa (29 x 106 psi)
Electrical Conductivity2.2 % IACS
Electrical Resistivity Order of Magnitude-6 10x Ω-m
Elongation at Break46 %
Modulus of Resilience (Unit Resilience)210 kJ/m3
Poisson's Ratio0.28
PREN (Pitting Resistance)27
Specific Heat Capacity500 J/kg-K
Strength to Weight Ratio81 kN-m/kg
Tensile Strength: Ultimate (UTS)640 MPa (93 x 103 psi)
Tensile Strength: Yield (Proof)290 MPa (42 x 103 psi)
Thermal Conductivity14 W/m-K
Thermal Diffusivity3.5 m2/s
Thermal Expansion13 µm/m-K
Unit Rupture Work (Ultimate Resilience)240 MJ/m3
The length of each bar compares the given value to the highest value in the database.
Iron (Fe)45.2 to 53.8 %
Chromium (Cr)24 to 26 %
Nickel (Ni)20.5 to 23.5 %
Molybdenum (Mo)1.6 to 2.6 %
Manganese (Mn)0 to 2.0 %
Silicon (Si)0 to 0.5 %
Nitrogen (N)0.090 to 0.15 %
Phosphorus (P)0 to 0.030 %
Carbon (C)0 to 0.020 %
Sulfur (S)
We can provide 310MoLN material in the form of flange, fittings, pipes, fasteners.