Refractory fire high alumina brick used for high temperature industry furnace
High aluminum brick is three oxide two aluminum (Al2O3) content is higher than 48% of the aluminum silicate refractory products.If the content of Al2O3 is higher than 90%, it is called corundum brick.Due to different resources, national standards are not completely consistent.For example, the lower limit of Al2O3 content for high alumina refractories in European countries is 42%.In China, according to the content of Al2O3 in high aluminum brick is usually divided into three classes :Ⅰ -Al2O3 content > 75%;Ⅱ et al --- the content of Al2O3 is 60 ~ 75%;Ⅲ et al ---the content of Al2O3 is 48 ~ 60%.A neutral refractory with an alumina content of more than 48%.It is formed and calcined from alumina or other raw materials with high alumina content.High thermal stability, refractoriness above 1770℃.Good slag resistance.Used for lining of electric steel-making furnace, glass furnace, cement rotary furnace, etc.
Production process: the production process of high-alumina bricks
and multi-clinker clay bricks is similar, the difference lies in
the higher proportion of clinker in the ingredients, up to 90 ~
95%, clinker before crushing needs to be sorted and screened to
remove iron, sintering temperature is higher, such as Ⅰ, high
alumina bricks with tunnel kiln firing is generally 1500 ~ 1600℃.
Application: It is mainly used for lining of blast furnace, hot
blast furnace, top of electric furnace, blast furnace, reflection
furnace and rotary kiln.In addition, high alumina brick is also
widely used as open hearse regenerative lattice brick, plug head
for gating system, nozzle brick, etc.But the price of high aluminum
brick should be higher than clay brick, so the place that can
satisfy the requirement with clay brick need not use high aluminum
brick.
Item | Technical Data | ||||
International code name | SK35 | SK36 | SK37 | SK38 | SK40 |
Al2O3 min % | 48 | 55 | 65 | 75 | 80 |
Fe2O3 max % | 2 | 2 | 2 | 2 | 2 |
Refractoriness °C min | 1750 | 1770 | 1790 | 1790 | 1790 |
Refractoriness under Load °C min | 1420 | 1470 | 1500 | 1520 | 1530 |
Permanent Linear Change % | 1420°C x 2h | 1500°C x 2h | 1500°C x 2h | 1500°C x 2h | 1500°C x 2h |
Apparent Porosity max % | +0.1~-0.4 | +0.1~-0.4 | +0.1~-0.4 | +0.1~-0.4 | +0.1~-0.4 |
22 | 22 | 23 | 23 | 21 | |
Cold Crushing Strength min | 39 | 44 | 49 | 54 | 65 |
Detail the classification of high aluminum brick
1, ordinary high aluminum brick
The main mineral composition of the refractory brick is quartz,
corundum and glass phase. With the increase of the content of Al2O3
in the product, mullite and corundum also increase, the glass phase
will decrease accordingly, and the refractory and high temperature
performance of the product will improve accordingly.Common high
aluminum brick has a series of better fire resistance than clay
brick, is a good application effect, widely used material, widely
used in a variety of thermal kiln.Compared with clay brick, it can
effectively improve the service life of kiln.
2, high charge soft high aluminum brick
Compared with ordinary high-alumina bricks, the difference between
high-alumina bricks and high-alumina bricks is the matrix part and
the binder part. In the matrix part, besides adding three-stone
concentrate, according to the theoretical composition that the
chemical composition after firing is close to mullite, the
high-alumina materials, such as corundum powder and high-alumina
corundum powder, are reasonably introduced.Binding agent selection
of high quality ball clay, according to the variety of different
clay composite binder, or mullite binder.By the above method, the
load softening temperature of high aluminum brick can be increased
by about 50~70℃.
3. Low creep high aluminum brick
The creep resistance of high alumina brick is improved by using the
so-called unequilibrium reaction.Namely according to the use of the
kiln temperature condition, three stone mineral is added in the
matrix, activated alumina, etc., the composition of the matrix near
or entirely of mullite, because the matrix of mullite
petrochemical, will improve the material of mullite content and
reduce, glass phase and mullite excellent mechanical and thermal
properties is conducive to improving the performance of high
temperature material.Controlling Al2O3/SiO2 is the key to complete
mullitization of the matrix.Low creep high alumina brick is widely
used in hot blast furnace, blast furnace and other thermal furnace.
4, phosphate combined with high aluminum brick
Phosphate-bonded high aluminum brick is a kind of chemical bonded
refractory brick which is made of dense super grade or first grade
high bauxite clinker as the main raw material, phosphate solution
or aluminum phosphate solution as the binder, after being pressed
by semi-dry method and heat treated at 400~600℃.It belongs to the
non-fired brick, in order to avoid the product contraction in the
process of use, the general need to introduce heating expansion raw
materials, such as blue pinstone, silica and so on.Compared with
the ceramic combination fired high aluminum brick, its anti-peeling
performance is better, but its load softening temperature is low,
anti-erosion performance is poor, so lag to add a small amount of
fused corundum, mullite, etc., to strengthen the
matrix.Phosphate-bonded high alumina brick is widely used in cement
rotary kiln, electric furnace top and other furnace parts.
5, micro expansion high aluminum brick
The main brick is high bauxite as the main stock material, adding
three stone concentrate, in accordance with the high aluminum brick
production process.To make a moderate amount of inflation in the
process of using high alumina brick, the key is to choose a good
three stone concentrate and its particle size, good control of
sintering temperature, make the choice of three stone mineral of
mullite petrochemical, part three residual stone mineral, the
remaining three stone mineral in use process further mullite
petrochemical (primary or secondary mullite petrochemical), along
with the volume expansion.The choice of three stone minerals to
composite materials as well.Because the decomposition temperature
of the three stone minerals is different, the expansion of mullite
is also different.Using this characteristic, the high alumina brick
has the corresponding expansion effect due to the different working
temperature, squeezes the brick seam, improves the overall
compactness of the lining body, and thus enhances the brick's
anti-slag penetration ability.
The above is the classification of high aluminum brick, if you are
interested in refractory materials, you can search on Baidu "find
refractory material network" for a detailed browse, more wonderful
articles and so on you see, we aim to provide more buyers and
sellers reasonable and fair trading platform, so that refractory
business is no longer difficult to do.
Packaging
1. 1 ton bags in container, 25 MT/20'FCL.
2. 25kg bags in container, 25 MT/20'FCL
3. 25kg bags in ton bags, then in container, 25 MT/20'FCL
4. as the customer' request
Packaging of SK37 High Alumina Refractory Brick
1.on wooden pallets with plastic cover: wooden pallet size :930*930
or 1000*1000mm,
2.Load weight of each pallet: 1.5-2.0 tons,
Shipping of SK37 High Alumina Refractory Brick
1.Our packaging is as per customer’s request
2.Normal goods delivered by sea transport
3.Sample shipping by express
4.We will shipping and delivery goods timely, quality and quantity
guaranteed, and also in accordance with the contract and customer's
requirement completely.
Delivery:
15-30 days working day for large quantity. The shipment we will
arrange as soon as possible. Of course, if it is a custom products,
the shipping time will delay.
Sample:
Usually by EMS, DHL, UPS, TNT, FedEx. Anyway you like. Bulk order: Usually by sea.
Payment:
It can be through T/T, L/C at sight. The specific terms determined
according to the quantity of the goods, etc.
Your inquiry related to our product & price will be replied
within 24 hours.
Export:
Our products have been exported to many countries: Australia,
Chile, USA, Russia, UK, Indonesia, etc., good quality have be
approved by our clients.
1.Timely response,
Timely response to your inquiry, multiple choice recommendations based on your demand,quickly respond mails and provide solutions.
2.Free sample of dry ramming mass
Sample and trial order are accepted for the quality evaluation
3.Strict quality control
Arrange production on time and control quality strictly.
4.Shorter delivery time.
Book the earliest vessel or plane to guarantee the delivery time.
5.Professional Services
Provide all the detailed news and pictures from order to delivery;offer relative export documents and original certificate if needed;warm and considerable after-sale service.
Henan hongtai kiln refractory co., LTD. : "quality first, reputation first, customer first: it is our
aim."Scientific management, strong technical force, perfect testing
means, advanced technological equipment and stable product quality
are the guarantee of quality service.Henan hongtai kiln
refractories co., LTD sincerely hopes to cooperate with you hand in
hand and in good faith.
Henan hongtai kiln refractory co., LTD. Main products are high alumina brick, clay brick, fused zirconium
corundum brick, fireproof ball lightweight insulation brick,
wear-resistant pouring material, corundum pouring material, low
cement high strength pouring material, impermeable material,
self-flowing material, plastic material, and various types of
refractory materials.For different industries, the cement industry
with anti-flaking high-alumina bricks, alkali resistant bricks,
phosphate bricks;Boiler industry USES all kinds of brand
wear-resisting brick, corundum brick, mullite brick and other
finalizing materials.The company insists on "product quality is the
life, enterprise integrity is the foundation", in the fierce market
competition, won many users' trust and praise.The products are sold
all over the country, as far as Vietnam, India, Korea, Pakistan,
kazakhstan, other southeast Asian countries and regions.
Customer visit :