4.5mm Red Singel Wall Halogen Free Flexible Heat Shrink Tubing
Ultra thin wall halogen free.flexible without adhesive and can be used easily.
High quality Heat shrink tubing without adhesive and with low moq short lead time from China manufacture.
Features
• Thin wall
• Halogen free
• Flame retardant well
• low smoke generation if burning
• Continuous operating
• Temperature:-55°C to 125°C
• Fully shrink temperature: 109°C
Dimensions
| Size | As Supplied | After Recovery | Standard Package | ||
| Inch | mm | Internal Diameter mm | Internal Diameter mm | Wall Thickness mm | Spool Length M/spooF |
| 1/16 | 1.0 | 1.4±0.2 | 0.65 | 0.20 | 200 |
| 1.5 | 1.9+0.2 | 0.85 | 0.20 | 200 | |
| 3/32 | 2.0 | 2.4±0.2 | 1.00 | 0.22 | 200 |
| 2.5 | 2.9±0.2 | 1.30 | 0.25 | 200 | |
| 1/8 | 3.0 | 3.4±0.2 | 1.50 | 0.28 | 200 |
| 3.5 | 3.9±0.2 | 1.80 | 0.28 | 200 | |
| 4.0 | 4.410.2 | 2.00 | 0.30 | 200 | |
| 3/16 | 4.5 | 4.9±0.2 | 2.30 | 0.30 | 100 |
| 5.0 | 5.5±0.2 | 2.5 | 0.32 | 100 | |
| 1/4 | 6.0 | 6.5±0.2 | 3.0 | 0.32 | 100 |
| 5/16 | 7.0 | 7.5±0.3 | 3.5 | 0.32 | 100 |
| 8.0 | 8.5±0.3 | 4.0 | 0.32 | 100 | |
| 3/8 | 9.0 | 9.5+0.3 | 4.5 | 0.35 | 100 |
| 10.0 | 10.5±0.3 | 5.0 | 0.35 | 100 | |
| 11.0 | 11.5±0.3 | 5.5 | 0.40 | 100 | |
| 1/2 | 12.0 | 12.5±0.3 | 6.0 | 0.40 | 100 |
| 13.0 | 13.5±0.3 | 6.5 | 0.40 | 100 | |
| 14.0 | 14.5±0.3 | 7.0 | 0.40 | 100 | |
| 5/8 | 15.0 | 15.5±0.4 | 7.5 | 0.40 | 100 |
| 16.0 | 16.5±0.4 | 8.0 | 0.40 | 100 | |
| 17.0 | 17.5±0.4 | 8.5 | 0.40 | 100 | |
| 3/4 | 18.0 | 18.5±0.4 | 9.0 | 0.42 | 100 |
| 20.0 | 20.5±0.5 | 10.0 | 0.45 | 100 | |
| 22.0 | 22.5±0.5 | 11.0 | 0.45 | 100 | |
| 1 | 25.0 | 25.5±0.5 | 12.5 | 0.45 | 50 |
Technical Data
| I Property I | Test Method | Typical Performance I |
| Tensile strength(MPa) | ASTM D 2671 | >10.4 |
| Ultimate elongation(%) | ASTM D 2671 | >200 |
| Tensile strength after heat aged (Mpa) | 158°CX168h | N7.3 |
| Ultimate elongation after heat aged (%) | 158°CX168h | ^100 |
| Longitudinal change(%) | ASTM D 2671 | -5%~+5% |
| Flammability | ASTM D 2671 C method | VW-1 |
| Dielectric strength (kV/mm) | ASTM D 149 | >15 |
| Volume resistivity (Q-cm) | ASTM D 876 | ^1014 |