New Energy Orange 20mm 25mm V0 Flame Retardant 2X Hea Shrink Tubing
150°c Flame retardant heat shrink tubing
Features
• 2:1 shrink ratio
• Flame retardant
• Good resistance to common fluids and solvents
• UL approved
• Continuous operating temperature:-55°C ~150°C
• Fully shrink temperature:135°C
• RoHS compliant
Dimensions
| Size | As Supplied | After Recovery | Standard Package | ||
| Inch | mm | Internal Diameter mm | Internal Diameter mm | Wall Thickness mm | Spool Lenqth M/spooF |
| 3/64 | 1.0 | N1.20 | W0.60 | 0.41±0.10 | 200 |
| 1/16 | 1.5 | 5=1.60 | W0.80 | 0.43±0.10 | 200 |
| 3/32 | 2.5 | N2.40 | W1.20 | 0.51±0.10 | 200 |
| 1/8 | 3.0 | N3.20 | ^1.60 | 0.5110.10 | 200 |
| 3/16 | 4.5 | ^4.80 | <2.40 | 0.51±0.10 | 100 |
| 1/4 | 6.0 | N6.4. | W3.20 | 0.64±0.10 | 100 |
| 3/8 | 9.0 | N9.50 | W4.80 | 0.64±0.10 | 100 |
| 1/2 | 12 | 5=12.7 | <6.40 | 0.64±0.10 | 100 |
| 3/4 | 18 | N19.1 | W9.50 | 0.76±0.15 | 100 |
| 1 | 25 | N25.4 | W12.7 | 0.89±0.15 | 50 |
| 5/4 | 32 | N32 | W15.9 | 0.8910.15 | 50 |
| 3/2 | 38 | N38 | W19.1 | 1.00±0.15 | 50 |
| 2 | 50 | N51 | <25.4 | 1.15±0.15 | 25 |
| 3 | 75 | N76 | W38.1 | 1.27±0.20 | 25 |
| 4 | 100 | N102 | W50.8 | 1.40±0.20 | 25 |
| 5 | 120 | >125 | W63.5 | 1.40±0.25 | 25 |
Technical Data
| I Property | Test Method | Typical Performance I |
| Tensile strength(MPa) | ASTM D2671 | 5=10.4 |
| Ultimate elongation(%) | ASTM D2671 | >200 |
| Tensile strength after heat aged(Mpa) | 180°CX168h | N7.3 |
| Ultimate elongation after heat aged (%) | 180°CX168h | >100 |
| Corrosion | UI224 | Pass |
| Flammability | ASTM D 2671C method | VW-1 |
| Voltage withstand | 2500V, 60s | No breakdown |
| Heat shock(%) | 250°CX4h | No cracks, flowing or dripping |
| Cold blend | -30°CX1 h | No cracks |
| Dielectric strength (kv/mm) | ASTM D 149 | N15 |
| Volume resistivity (Q-cm) | ASTM D 876 | ^1014 |
| Water absorption(%) | UL224 | <0.5 |