— Stainless Steel Coil —
Description
Product Name | 201 304 309S Grade 201 Grade Stainless Steel Coil |
Length | as required |
Width | 3mm-2000mm or as required |
Thickness | 0.1mm-300mm or as required |
Standard | AISI,ASTM,DIN,JIS,GB,JIS,SUS,EN,etc |
Technique | Hot rolled / cold rolled |
Surface Treatment | 2B,BA(bright annealed) NO.1 NO.2 NO.3 NO.4,8K HL(Hair Line) PVC |
Thickness Tolerance | ±0.01mm |
Material | 201, 202, 301, 302, 303, 304, 304L, 304H, 310S, 316, 316L, 317L,
321,310S 309S, 410, 410S,420, 430, 431, 440A,904L |
Application | It is widely used in high temperature applications, medical
devices, building materials, chemistry, food industry, agriculture, ship components. It also applies to food, beverage packaging, kitchen supplies, trains, aircraft, conveyor belts, vehicles, bolts, nuts, springs, and screen. |
MOQ | 5ton , We can accept sample order. |
Shipment Time | Within 15-20 workdays after receiving deposit or L/C |
Export Packing | Waterproof paper, and steel strip packed. Standard Export Seaworthy Package.Suit for all kinds of transport,or as required |
Capacity | 250,000 tons/year |
Chemical Composition and Mechanical Property
| Grade | C(%) | Si(%) | Mn(%) | P(%) | S(%) | Cr(%) | Ni(%) | N(%) | Cu(%) |
| 304 | ≤0.08 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 18.00-20.00 | 8.00-10.50 | ≤0.10 | / |
| 304L | ≤0.03 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 18.00-20.00 | 8.00-10.50 | ≤0.10 | / |
| 304H | 0.04-1.00 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 18.00-20.00 | 8.00-10.50 | ≤0.10 | / |
| Grade | Tensile Strength (Mpa) | Yield Strength (Mpa) | Elongation (%) | Rate Of Reduction In Area (%) | Density (G/Cm3) | Hardness (HB) (HRB) (HV) |
| 304 | ≥515 | ≥205 | ≥40 | / | 7.93 | ≤201HBW;≤92HRB;≤210HV |
| 34L | ≥515 | ≥205 | ≥40 | / | 7.93 | ≤187HB; ≤90HRB; ≤200HV |
| 304H | ≥515 | ≥205 | ≥40 | / | 7.93 | / |
| Grade | C(%) | Si(%) | Mn(%) | P(%) | S(%) | Cr(%) | Ni(%) | Mo(%) | Cu(%) |
| 316 | ≤0.08 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 16.0-18.00 | 10.00-14.00 | 2.00-3.00 | / |
| 316L | ≤0.03 | ≤1.00 | ≤2.00 | ≤0.045 | ≥0.15 | 16.0-18.00 | 10.0-14.00 | 2.00-3.00 | / |
| Grade | Tensile Strength (Mpa) | Yield Strength (Mpa) | Elongation (%) | Rate Of Reduction In Area (%) | Density (G/Cm3) | Hardness (HB) (HRB) (HV) |
| 316 | ≥620 | ≥310 | ≥30 | ≥40 | 7.98 | ≤187HB;≤90HRB;≤200HV |
| 316L | ≥620 | ≥310 | ≥40 | ≥60 | 7.98 | ≤187HB; ≤90HRB; ≤200HV |
Product Details
Production line
Our Warehouse
Packaging & Shipping
Application
Certificate:
Contact
Jiangsu Lianzhong Metal Products (Group) Co.,Ltd
sales03@jslzsteel.com
Mob:+8615251641660
Wechat:15251641660
WhatsApp:+8615251641660