Transparent Slip Fusible Molding Hot melt adhesive film fused interlining for garment
EVA adhesive film
Base material: single silicon release paper product specification:
thickness 0.04-0.25mm hot melt adhesive: EVA pressing temperature
Temperature: 110-130 ℃
Pressing time: 6-10s application scope: pet leather non woven
fabric wood paper and other bonding fields
PA film
Base material: single silicon release paper product specification:
thickness 0.05-0.25mm hot melt adhesive: PA pressing temperature:
150-180 ℃
Pressing time: 12-20s application scope: embroidery BADGE /
trademark back glue and other fields
PES film
Base material: single silicon release paper product specification:
thickness 0.05-0.25mm hot melt adhesive: PES pressing temperature:
140-160 ℃
Pressing time: 12-18s application scope: conductive cloth,
embroidery BADGE / textile label back glue, flocking transfer,
textile fitting, PVC high-frequency fitting and other fields.
TPU adhesive film
Product Name: hot melt adhesive membrane
TPU film
Base material: single silicon release paper product specification:
thickness 0.05-0.25mm hot melt adhesive: TPU pressing temperature:
120-150 ℃
Pressing time: 10-20s curing speed: 4min bonding range: nylon
fabric, polyester fabric, blend, wool, pure cotton, TPU, paper and
other materials; Composite processing of cotton yarn, nylon cloth,
Lycra cloth and other elastic fabrics; Nylon fabric, polyester
fabric, blended, pure cotton, leather, ABS and other materials.