Unionfull (Insulation) Group Ltd. |
Verified Suppliers
|
|
0.9mm White Polyurethane PU Coated Fiberglass Cloth For Welding
Blanket
This fabric is made from woven fiber glass cloth and
then coated with white polyurethane coating on both
sides. Total weight of this PU coated glass fabric is 900g/m2.
Basic cloth is 8HS fiberglass fabric. It
is 600g/m2 and 0.6mm thick. When coated with 150g/m2
PU coating each side, totally weight per unit can be 900gsm,
and thickness will be 0.9mm.
Usually common coated fiberglass fabric like silicone/PVC coated
fabric can be used below 260℃. While PU coating can work
under instantaneous temperature up to 1100 degree Celsius. So it is very suitable for welding protection, good for fire
blanket/curtain. Whats's more, PU coated fiberglass fabric also
have good properties like chemical resistance, high
strength, non itchy, colorful coating.
UPPE-8660D300:
Item | 666 PU Coated Fiberglass Fabric |
Total weight | 900 g/m2 |
Thickness | 0.9 mm |
Color | White |
Temperature | Coating: -50℃ to +260℃ |
Coating | Polyurethane Coating On Both Sides, 150/150 |
Width | 100cm, 127cm |
Properties:
Application:
Picture:
Data Sheet Of Basic Cloth 666:
Style | Weave | Count | Yarn | Weight | Thickness |
666 | 8HS | 41/33 | ECG 150 3/2 | 600g/m2 | 0.6mm |
8HS Satin Weave:
The eight harness satin is similar to the four harness satin. One
weft yarn floats over seven warp yarns and under one. This is
a flexible weave and common application of this weave type is for forming
over curved surfaces.
666 fiberglass fabric is a heavy duty basic cloth and is usually
used for fire blanket. When coatded with PU coating(PU coating can
resist 1100℃ for a short time), this coated 666 fabric is very
suitable for welding blanket. Especially for welding splash
protection.