Thermal Spraying Al Wire 3.1mm / 4.7mm
| Chemical Composition | Tensile Strength(Mpa) | Elongation% |
| Al>99.6% | 97-113 | 3.20 |
1. Stainless Steel
| Brand | Chemical Composition |
| 1Cr13 | Cr 13 |
| 2Cr13 | |
| 3Cr13 | |
| 4Cr13 | Ni, Cr, Mo |
| 316L | Ni, Cr, Mo |
| 1Cr18Ni9Ti | Cr 18 Ni9 |
2. NIAl alloy solid wire (Monel)
Our company use Vacuum furnace and casting control to make the NiAl alloy solid wire, it is specially used for arc spray boning layer. This wire has stable chemical composition, low oxygen and high bonding strength.
| Chemical Composition | Coating Strength (Mpa) | Melting temp (℃) | Coating Hardness(HRC) |
| Ni95%Al5% | 65-68 | 1010 | 23-25 |
Applying technique: Arc spray
Specification of wire: 1.6mm, 2.0mm, 15kg/spool
| Chemical Composition | Coating Strength (Mpa) | Melting temp (℃) | Coating Hardness(HRC) |
| Ni, Cr, Ti | 48 | 1450 | 45 |
Characteristic: Strong Resistance to high temperature corrosion oxidation
Application: Boiler water wall tube, fan blade
| Material brand | Composition | Characteristic | Application |
| HCF-50 | Ni, Cr, Ti | Coating Strength ≥48Mpa Coating Hardness≥HRC46 The best resistance of oxidation, high temperature and corrosion | Boiler water wall, superheater anti-corrosion and anti-oxidation, steam turbine blade, steel plant heat and corrosion resistance |
| HCF-95 | Ni, Al, Ti | Coating Hardness≥75Mpa Strong anti-oxidation and corrosion resistance | High temperature prime material |
| HCF-25 | Ni, Cr, W,Mo | Coating Strength≥45Mpa Coating Hardness≥HRC33 Strong anti-oxidation and corrosion resistance | Boiler "four tubes" anti-wear, shaft, pump, drum, dryer and other anti-corrosion and anti-wear |
HCF-40 NiCrTiFe | Ni, Cr, W,Mo | Coating Strength≥47Mpa Coating Hardness≥HRC43 High temperature, oxidation, corrosion resistance | Anti-oxidation Corrosion in Pressure Vessels |
HCF-80 CL-NiCr | Ni, Cr | Coating Strength≥40Mpa Coating Hardness≥HRC35 Good corrosion resistance | Corrosion protection of water wall, superheater and reheater |
| HCF-01 | W, Al, Fe | Coating Strength≥40Mpa Coating Hardness≥HRC35 Certain anti-oxidation and corrosion resistance | Anti-oxidation Corrosion at Lower Temperature |
| Monel | Ni, Cu, Al | Hydrogen sulfide resistance, sulfuric acid resistance, hydrochloric acid resistance
| Used for repairing various hydrogen sulfide resistant, acid resistant containers, wear resistant and spare parts |
| Chemical Composition | Coating Strength (Mpa) | Melting temp (℃) | Coating Hardness(HRC) |
| Ni95%Al5% | 65-68 | 1010 | 23-25 |