Product Introduction :
HR-7001LB/HR-7010 Gray Cationic Epoxy Electrocoat for auto is the 8th generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd. in cooperation with Germany HS International Chemical Industry Group.
It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal,
such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products, zinc-aluminum alloy sheet and stainless steel sheet etc
This product features shown below:
The appearance of the coating is flat, delicate, smooth.
Good stability of bath can adaptable for a longer updating cycle.
The bath has strong anti-shrinkage and anti-pollution ability.
suitable for auto body industry, such as cars, SUV and other models
The main component :
Solvent: alcohol ether
Neutralizing agent: organic acid
Curing agent: totally enclosed multi-isocyanates
The main supplier:
Material name | Supplier |
Bisphenol A epoxy resins
| Formosa Plastic Group / Kukdo / Dow Chemical |
Amine hardendner
| INTERSCAN / Huntsman Corporation |
Titanium pigment
| DuPont |
Product film performance :
| Project | Indicator | Test standard | |
| Appearance | Normal / Abnormal | Normal | Ocular estimate |
| Hardness | ≥ | 2H | GB/T 6739 |
| Cup drawing | mm,≥ | 6 | GB/T 9753 |
| Adhesion | level | 0 | GB/T 9286 |
| Flexibility | mm | 1 | GB/T 1731 |
| Impact | Kg.cm | 50 | GB/T 1732 |
| Gloss | 60° | 50-80 | GB/T 9754 |
| Water resistance | h,(23±2)℃ ≥ | 240 | GB/T 1733 |
| Acid resistance | h(0.05N H2SO4) ≥ | 72 | GB/T 9274 |
| Alkali resistance | h(0.1N NaOH) ≥ | 72 | GB/T 9274 |
| Gasoline resistance | 93#,24h | No bubbles, no wrinkles, no rust, no shedding | GB/T 9274 |
| Interlayer adhesion | ≤level | 1 | GB/T 9286 |
| *Salt spray resistance | film thickness ≥ 20μm | 1000 | GB/T 1771 |
| Stone strike resistance | level ≤ | 3.0 | Q/DFLCM 5466 |
* Note: The substrate use the Bonder standard phosphating steel
panel, crossed out unidirectional expansion eclipse ≤ 2mm.