High throwing power (Four-box method) penetration white electrophoresis paint
Product Introduction :
HS-6060ALB/HS-6600 White Cationic Epoxy Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd.
It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal,
such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products, zinc-aluminum alloy sheet and stainless steel sheet etc.
This product features shown below:
Excellent leveling coating,good bonding force and compatibility with plastic powder | |
Good stability of bath can adaptable for a longer updating cycl | |
| Strong anti-corrosion properties, good salt spray resistance workpiece edge. |
Main ingredients:
| 1,Neutralizing agent: organic acid |
| 2,Pigment: titanium dioxide, kaolin,antirust pigment |
| 3,Additives: surface active agent, prevent shrinkage cavity agent |
Filling tank proportion and method:
⑴ Bath preparation
Ratio:
Resin 750.00-1000.00
Paste 250.00
DI water 1900.00-2200.00
Total 3 3025.00-3575.00
⑵ Ripening conditions
Sample quantity: 3000-4000g
Container: 5L (Diameter 16cm)
Tank temperature:28-30 ℃
Time: 24～48Hr
Mixed conditions: impeller diameter 8cm (speed 200rpm)
(3) Coating conditions
Experimental panel: phosphated cold-rolled steel plate
Tank temperature: 28-34 ℃
Pole ratio: A/C = 1/2 ~ 1/4
Distance of electrodes: 15cm
ED time: For full immersing 1-3 minutes ( 20 seconds soft start)
Baking conditions:(165-175)℃×(20-30)min (Keeping temperature of parts coated)
Bath on site management project:
Good bath data and coating quality, from the strict parameters management and maintenance of equipment, production line according to its own reality time situation, can have different management project and specifications, recommend the construction parameters see the table below for reference:
| Classification | Project | Control Data | Testing frequency | |
| New bath | Anolyte | |||
| Electrophoresis tank | Ratio | 1:(3-4) | -- | |
| Ripening time | 24-48 | -- | ||
| Solid ( 120 ℃ /1h ,% ) | 14±4 | -- | once a day | |
| PH | 5.6-6.4 | 2.0-3.5 | once a day | |
| Conductivity ( μs/cm ) | 1200±400 | 1500±500 | once a day | |
| P/B | 0.25-0.35 | once a week | ||
| Throwing power (Four-box method), ≥ | ≥60% | once a year | ||
| Solvent content (%) | 0.8-1.5 | once a week | ||
| Liquid level Fall head (cm ) | 10-15 | once a day | ||
| ED voltage( V ) | 0-300 | once a day | ||
| Break voltage ( V ) | ≥320 | once a week | ||
| Bath temperature ( ℃ ) | 28-34 | once a day | ||
| ED time( S ) | 60~180 | once a day | ||
| UF － 1 Tank | Solid content (%) | ≤2.0 | once a day | |
| UF － 2 Tank | Solid content (%) | ≤0.8 | once a day | |
| Baking furnace | Provisions furnace temperature( ℃ ) | 170-180 | once a day | |
| Curing conditions | Drying temperature | (165-175) ℃ ×(20-30)min (With content holding time) | once a day | |
Specification statement:
This manual contains information and recommendations are based on our current knowledge and experience, accurate to the date of publication so far. It cannot be used as a guarantee or commitment, in any case, responsibility for users to decide on the use of this product is intended availability. We remain in the process or new development within the scope of the right to change product specifications. Because we cannot control the construction conditions, hope through customers own experiments to determine satisfaction with the final results.
If you want to learn more about HLS coating products, please contact Sales Department of Shanghai HLS now