ASTM B704 Alloy 825 Nickel Alloy Welded Coiled Tubing For Control Line
Grade: Alloy 625/UNS N06625, Alloy 825/UNS N08825 etc.
OD: 2.38-25.4mm
WT: 0.51-2.65mm
Length: ＜10000 m/coil
Chemical composition
| % | Ni | Cr | Mo | Fe | C | Mn | Si | P | S | Co | Nb+Ta | Al | Ti |
| min | 58.0 | 20.0 | 8.0 | 3.15 | |||||||||
| max | 23.0 | 10.0 | 5.0 | 0.10 | 0.50 | 0.50 | 0.015 | 0.015 | 1.00 | 4.15 | 0.40 | 0.40 |
Physical properties
| Density | 8.44 g/cm3 |
| Melting range | 1290-1350℃ |
Features: Alloy 625 has excellent strength at temperatures up to 816℃. At higher temperatures, its strength is generally lower than that of other solid solution strengthened alloys. Alloy 625 has good oxidation resistance at temperatures up to 980℃ and shows good resistance to aqueous corrosion, but is relatively moderate compared to other more capable corrosion resistant alloys.
Applications: Chemical process industry and sea water application. Alloy 625 is used in short term applications at temperatures up to 816℃. For long term service, it is best restricted to a maximum of 593℃, because long term exposure above 593℃ will result in significant embrittlement.
MTSCO has 26 cold-drawing production lines. And the annual production capacity is 5000 tons, the annual GDP is more than 30 million USD.
1 . Seamless tube : small diameter seamless overlength coiled tubing , bright annealed tube , inside and outside polished tube , heat exchanger tube , U-bent tube , the products all adopt the most advanced technology , with 26 production lines .
2 . Seamless pipe : MTSCO has 8 production lines for stainless steel cold drawn pipe , 10 production lines for cold roll pipe .
3 . Other Products : Stainless steel welded pipe , flange and fitting are our relevant products , for providing our clients the supplied solutions of the pipeline projects .