DLX FeCrAl 0Cr25Al5 Iron Chromium Aluminium Electric Heating Electric Stove Wire

Country/Region	china
City & Province	changzhou jiangsu
Categories	Electrical Wires

Product Details

Product Description

DLX FeCrAl 0Cr25Al5 iron chromium aluminium Electric heating electric stove wire

1. Introduction to products
FeCrAl alloy is a ferritic iron-chromium-aluminium alloy with high resistivity and has superior oxidation resistance for use at temperatures up to 1450 centigrade degree., as compared to other commercial Fe and Ni base alloy.

2. Application
Our Products are widely applied to chemical industry, metallurgy mechanism, glass industry, ceramic industry, home appliance area and so on.

Whether the electric furnace wire is durable or not is not the thicker the more durable it is.The length of a single straight wire is calculated according to the voltage and power required by the buyer, and then according to the size of the installation site, whether the straight wire can

meet the installation requirements, and finally according to compliance The electric furnace wire required for installation calculates that the surface load is controlled within a reasonable range

Alloy Nomenclature Performance		1Cr13AL4	0Cr25Al5	0Cr21AL6	0Cr23Al5	0Cr21Al4	0Cr21Al6Nb	0Cr27Al7Mo2
Main Chemical composition	Cr	12.0-15.0	23.0-26.0	19.0-22.0	20.5-23.5	18.0-21.0	21.0-23.0	26.5-27.8
	Al	4.0-6.0	4.5-6.5	5.0-7.0	4.2-5.3	3.0-4.2	5.0-7.0	6.0-7.0
	Re	opportune	opportune	opportune	opportune	opportune	opportune	opportune
	Fe	Rest	Rest	Rest	Rest	Rest	Rest	Rest
							Nb0.5	Mo1.8-2.2
Max. continuous service temp. of element(°C)		950	1250	1250	1250	1100	1350	1400
Resistivity at 20ºC(μΩ·m)		1.25	1.42	1.42	1.35	1.23	1.45	1.53
Density(g/cm3)		7.4	7.1	7.16	7.25	7.35	7.1	7.1
Thermal conductivity(KJ/m·h·ºC)		52.7	46.1	63.2	60.2	46.9	46.1	--
Coefficient of lines expansion(α×10-6/ºC)		15.4	16	14.7	15	13.5	16	16
Melting point approx.( ºC)		1450	1500	1500	1500	1500	1510	1520
Tensile strength(N/mm2)		580-680	630-780	630-780	630-780	600-700	650-800	680-830
Elongation at rupture(%)		>16	>12	>12	>12	>12	>12	>10
Variation of area(%)		65-75	60-75	65-75	65-75	65-75	65-75	65-75
Repeat Bending frequency(F/R)		>5	>5	>5	>5	>5	>5	>5
Hardness(H.B.)		200-260	200-260	200-260	200-260	200-260	200-260	200-260
continuous service time(Hours/ ºC)		--	≥80/1300	≥80/1300	≥80/1300	≥80/1250	≥50/1350	≥50/1350
Micrographic structure		Ferrite	Ferrite	Ferrite	Ferrite	Ferrite	Ferrite	Ferrite
Magnetic properties		Magnetic	Magnetic	Magnetic	Magnetic	Magnetic	Magnetic	Magnetic