Inconel625 / NS336 / N06625 / NiCr22Mo9Nb / NA21 / NC22DNb / 2.4856 Cold Rolled Coils
Inconel625/NS336/N06625/NiCr22Mo9Nb/NA21/NC22DNb/2.4856 T0.1-1.0mm W 4-250mm Surface 2B HV 240-280 (Or Customized)
Applications:
Usage example: Suitable for manufacture aero-engine components, aerospace structural components, chemical equipment and contact with seawater and exposed to high mechanical stress occasions.
Description:
Inconel 625 is a nickel-chromium-molybdenum alloy, there is a small amount of niobium, for enhancing the hardness of the alloy, this alloy does not require heat treatment can be increased by the very high strength. This alloy to resist corrosion in a variety of harsh acidic environment,pitting and crevice corrosion This alloy used in chemical processing, aerospace, marine engines, pollution control equipment, and nuclear reaction device.
Inconel nickel chromium alloy 625 is used for its high strength, excellent fabricability (including joining), and outstanding corrosion resistance. Service temperatures range from cryogenic to 1800°F.
Specifications:
Thickness:0.1—1.0mm Usually 0.10mm 0.8mm
Width:4.00—250mm Usually 38.1mm 31.25mm
Tolerance: +/-0.01mm.
Other specifications can be customized
Surface:2B
Hardness:240—280HV(As order’s requirements)
MOQ:1 tons
Port of Loading:Shanghai
Payment:T/T
Delivery time: 35-45 working days after signing the contract
Chemical composition:
Alloy | C | Si | Mn | Fe | S | Ni | Cr | Mo | P | Co | Ti | Al |
Inconel625 | ≤0.10 | ≤0.50 | ≤0.50 | ≤5.00 | ≤0.015 | ≥58 | 20-23 | 8-10 | ≤0.015 | ≤1.0 | ≤0.4 | ≤0.4 |
Mechanical Character:
Density | Melting range | Tensile strength | Yield strength | Elongation | Coefficient of elasticity | Hardness |
8.44 g/cm3 | 1290 - 1350 ℃ (2350 - 2460 oF) | 930MPa | 517MPa | 42.50% | 207GPa | 190 HB |
Competitive Advantage:
Main characteristics: Resistance to corrosion and oxidation resistance, low temperature to 980 ℃ with good tensile and fatigue properties, and resistance to stress corrosion in salt fog atmosphere.