Product name:ZAMAK COFFIN DECORATION
Other name: metal ring screw
Model: D025
Brand: B&R
Application: European style coffin
Origin: China
Manufacturer: Sumer International (Beijing) Trading Co.,Ltd
Product detail:
Size: diameter 4cm
Material: Zamak (Zinc alloy)
Color: Gold, Silver or Bronze (Optional)
Attached on coffin by screw
MOQ:1000 pcs
Packing: Carton
Main feature:
Professionally engaged in funeral field over 10 years;
Customized products acceptable;
Good quality and competitive price;
More Information:
Zamak 5 composition per standard
Zamak 5 has the same composition as zamak 3 with the addition of 1% copper in order to increase strength (by approximately 10%), hardness and corrosive resistance, but reduces ductility.It also has less dimensional accuracy.Zamak 5 is more commonly used in Europe.
Zamak 5 properties
| Property | Metric value | Imperial value |
| Mechanical properties | ||
| Ultimate tensile strength | 331 MPa (270 MPa aged) | 48,000 psi (39,000 psi aged) |
| Yield strength (0.2% offset) | 295 MPa | 43,000 psi |
| Impact strength | 52 J (56 J aged) | 38 ft-lbf (41 ft-lbf aged) |
| Elongation at Fmax | 2% | |
| Elongation at fracture | 3.6% (13% aged) | |
| Shear strength | 262 MPa | 38,000 psi |
| Compressive yield strength | 600 MPa | 87,000 psi |
| Fatigue strength (reverse bending 5x108 cycles) | 57 MPa | 8,300 psi |
| Hardness | 91 Brinell | |
| Modulus of elasticity | 96 GPa | 14,000,000 psi |
| Physical properties | ||
| Solidification range (melting range) | 380—386 °C | 716—727 °F |
| Density | 6.7 kg/dm3 | 0.24 lb/in3 |
| Coefficient of thermal expansion | 27.4 μm/m-°C | 15.2 μin/in-°F |
| Thermal conductivity | 109 W/mK | 756 BTU-in/hr-ft2-°F |
| Electrical resistivity | 6.54 μΩ-cm at 20 °C | 2.57 μΩ-in at 68 °F |
| Latent heat (heat of fusion) | 110 J/g | 4.7x10−5 BTU/lb |
| Specific heat capacity | 419 J/kg-°C | 0.100 BTU/lb-°F |
| Coefficient of friction | 0.08 | |
Zamak 7
Zamak 7 has less magnesium than zamak 3 to increase fluidity and ductility, which is especially useful when casting thin wall components. In order to reduce inter-granular corrosion a small amount of nickel is added and impurities are more strictly controlled.
Zamak 7 composition per standard
| Alloying elements | Impurities | |||||||||||
| Standard | Limit | Al | Cu† | Mg | Pb | Cd | Sn | Fe | Ni‡ | Si | In | Tl |
| ASTM B240 (Ingot) | min | 3.9 | - | 0.01 | - | - | - | - | - | - | - | - |
| max | 4.3 | 0.1 | 0.02 | 0.002 | 0.002 | 0.001 | 0.075 | - | - | - | - | |
| ASTM B86 (Cast) | min | 3.5 | - | 0.005 | - | - | - | - | 0.005 | - | - | - |
| max | 4.3 | 0.25 | 0.02 | 0.003 | 0.002 | 0.001 | 0.075 | 0.02 | - | - | - | |
| GB8738-88 | min | 3.9 | - | 0.01 | - | - | - | - | 0.005 | - | - | - |
| max | 4.3 | 0.1 | 0.02 | 0.002 | 0.002 | 0.001 | 0.075 | 0.02 | - | - | - | |
| †Impurity ‡Alloying element | ||||||||||||
More Picture:
D025 gold color zamak ring (screw)
Bronze and gold coffin screw ring zinc alloy
Different zamak screws in bronze color