125℃ Self-cross linking LSZH FRPolyolein Cable Compound
ZC-SC125P |
| General lnformation |
| Description |
| ZC-SC125P is a self-crosslinking low smoke zero halogen flame
retardant polyolefin cable compound, which can be naturally
cross-linked after being extruded into a cable. This product is
mainly used for the sheath and insulation of photovoltaic cables
that comply with TUV2Pfg-1169 and EN50618. |
| |
| Standard |
| 1) EN50618-2014 |
| 2) 2Pfg1169/08-2007 |
| 3) IEC60332-1-2-2015 |
| |
| Specifications |
| High temperature resistance XLPO Compound for wires and cables up
to 3KV. |
| |
| Specification Sheet |
| Product Properties |
| | Unit | Test method | Standard
Value | Typical
Value |
| | | Nation | International |
| Density | g/cm3 | GB/T 1033 | ISO 1183-1 | ┄ | 1.40 |
| Tensile strength | Mpa | GB/T 1040.2 | ISO 527-2 | ≥10.0 | 13.5 |
| Elongation at break | % | ≥150 | 250 |
Air ageing
(158±2℃,
168h) | Change of
tensile strength | % | GB/T 2951.12 | IEC 60811-1 | ±25 | +12 |
|
Change of
elongation | % | ±25 | -8 |
|
| Volume resistivity (20℃) | Ω·m | GB/T 1410 | IEC 60093 | ≥1.0x1012 | 2.6x1012 |
| Volume resistivity at operating temperature (125±2℃) | Ω·m | ┄ | ┄ | ≥2.0x108 | 3.5x108 |
|
| Dielectric strength | MV/m | GB/T 1408.1 | IEC 60243-1 | ≥20 | 25 |
| Brittleness temperature (-40℃) | ℃) | GB/T 5470 | ISO 974 | Pass | Pass |
Hot set
elongation
(200℃,
0.2Mpa,
15min) | Elongation
under load | % | GB/T 2951.21 | IEC
60811-2-1 | ≤100 | 45 |
|
Permanent
deformation | % | ≤25 | 0 |
|
Water
Immersion test
(70℃, 168h) | Change of
tensile strength | % | GB/T 32129 | ┄ | ±30 | -3 |
|
Change of
elongation | % | ±35 | -6 |
|
| | | | | | | | | | | | | | | | |
| Product Properties |
| | Unit | Test method | Standard
Value | Typical
Value |
| | | Nation | International |
| Oxygen index | % | GB/T 2406.2 | ISO 4589-2 | ≥28 | 35 |
Smoke
density | non-luminous flame | | GB/T 8323.2 | ISO 5659-2 | ≤350 | 310 |
| flame combustion | ≤100 | 70 |
| HCl and HBr content | % | GB/T 17650 | IEC 60754 | ≤0.5 | 0 |
| HF content | % | ≤0.1 | 0 |
| pH value | ┄ | ≥4.3 | 5.0 |
| Conductivity | μS/mm | ≤10 | 1.1 |
| | | | | | | | | | | | | | | | |
NOTE: (1)The toxicity of smoke produced by materials shall be
negotiated by both the supplier and the demander
according to the needs of the product application.
(2)Thetechnicalindicatorsspecifiedinthetablearethevaluesobtainedaftercrosslinking. |
| Additional Information |
| Processing Techniques: |
Extruding techniques
It is recommended to use a low smoke zero halogen special screw,
with a length to diameter ratio of L/D=20~25 and a compression
ratio of 1.1~1.3. Because the actual temperature of the melt is
related to the length diameter ratio, compression ratio and screw
structure of the extruder, the appropriate extrusion temperature
should be selected according to the specific situation of the
extruder.
The recommended setting temperatures for each zone of the extruder
are as follows: |
| Zone | Z1 | Z2 | Z3 | Z4 | Head | Die |
| Temperature(℃) | 120 | 130 | 140 | 140 | 150 | 150 |
| |
| Using |
(1)When using this product, mix the A and B components evenly and
drop them into the hopper.
If color is required, the cable factory can use polyethylene base
color masterbatch and materials
within 8 hours after unpacking.
(2)This product should not be shut down for a long time. If it is
shut down for a long time, it is
recommended to stop and clean the screw before starting up again.
(3)To ensure sufficient crosslinking of the material, it is
recommended that the cable be placed in
a 70°C water bath or steam room for 6~8h, or at a constant
temperature and humidity (23°C, 50%)
for 7 days. The specific placement time is adjusted according to
the thickness of the product and
the crosslinking degree of the material, so as to meet the
performance requirements of the cable. |
| Package.Storage and Transport: |
| Package | Net weight | The A and B component are kept in different bags, net weight of
A component is 25kg and B component is 5kg |
|
| Method | Aluminum foil/polyethylene complex film bag for inner+ PP woven
bag/
PE/Kraft paper bag for outer |
|
| Transport | Requirement | Keep away from the sunshine, rain and soaking during transport, as
well
as handle gently during carrying. |
|
| Storage | Environment | clean, dry and ventilated warehouses |
| Warranty | 6 months |