Konica Digital Printing PVC Sheet for pvc card production
1. Konica Digital Printing PVC Sheet for pvc card production- Introduction
Konica Digital printing PVC sheet MDP-KM-W is suitable for Konica Minolta digital printer series. It could be printed directly by Konica printers with perfect printing quality.
● Suitable for the whole series of Konica Minolta printers.
● High definition images.
● No crack occurs on the printed images after lamination at high temperature.
2. Konica Digital Printing PVC Sheet for pvc card production- Parameters:
| Size | A4, A3 or as per customer requirements (tolerance +/-0.5mm) |
| Thickness | 0.15mm-0.40mm |
| Color | Common white/supper white |
| Package method | 100 or 200 sheets/package. |
| Storage condition | Sealed, moisture-proof, room temperature under 40℃ |
Thickness range: 0.15-0.40mm
Color: White
Application: All kinds of cards
Size(mm): Rolls or customized sheets
3. Konica Digital Printing PVC Sheet for pvc card production-Application
Digital printing sheet, also called electronic ink printing sheet, it is a novel material used for digitization ink printing, and its color is recovered accurately. Printing ink has strong adhesive force, high laminating strength, clear graphic outline, and free from static electricity. Generally, it is matched with tape film for making laminated card.
4. Konica Digital Printing PVC Sheet for pvc card production- Packing
| Product Test Report | |||||
| Product Name: PVC Digital Printing Sheet | |||||
| Inspected Items | Unit | Inspection Standard | Test Result | ||
| Appearance | The color is even, No black impurity spots, No obvious scratch | Meet the requirements | |||
| Length | mm | ±1 | OK | ||
| Width | mm | ±1 | OK | ||
| Thickness | mm | ±10% | OK | ||
| Squareness | mm/m | ≤1 | 0.4 | ||
| Density | g/cm3 | 1.42±0.05 | 1.41 | ||
| Chromatic aberration | ∆E | ≤1.0 | 0.51 | ||
| Pulling Strength | MD | MPa | ≥45 | 47 | |
| CD | ≥43 | 43.1 | |||
| Roughness Ra | 4# | ṷ m | 0.7～1.8 | 1.28 | |
| 5# | ṷ m | 0.7～1.8 | 0.97 | ||
| Roughness Rz | 4# | ṷ m | 4～12 | 7.912 | |
| 5# | ṷ m | 4～12 | 6.91 | ||
| Surface Tension | 4# | Dynes/cm | ≥34 | 34.5 | |
| 5# | ≥34 | 34 | |||
| Heating shrinkage rate | MD | % | ≤-6.0 | -2 | |
| CD | ≤+2.2 | 0 | |||
| Whiteness | 96.2 | ||||
| Transmittance | % | 5.5 | |||
| Vicat softening point | ℃ | 78±2 | 78.9 | ||